برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | -- | ASTM D792 | 0.928 g/cm³ |
| density | -- | ISO 1183 | 0.930 g/cm³ |
| viscosity number | | ISO 307 | 2300 cm³/g |
| ElongationalStressF | | ISO 1152-2 | 0.240 MPa |
| intrinsic viscosity | | ISO 1628-3 | 20 dl/g |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shore hardness | 邵氏D,15秒 | ISO 868 | 60 |
| ball-indentation hardness | | ISO 2039-1 | 36.0 MPa |
| Shore hardness | 邵氏D | ASTM D2240 | 63 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| coefficient of friction | Steel - Dynamic | 内部方法 | 0.10 |
| Wear factor | 砂浆法 | 内部方法 | 100 |
| Wear amount | | 内部方法 | 100 |
| Tensile modulus | 23°C | ASTM D638 | 703 MPa |
| Tensile modulus | -- | ISO 527-2/1A/1 | 680 MPa |
| tensile strength | 屈服,23°C | ASTM D638 | 21.4 MPa |
| tensile strength | Yield | ISO 527-2/1A/50 | 20.0 MPa |
| Tensile strain | Yield | ISO 527-2/1A/50 | 13 % |
| Nominal tensile fracture strain | | ISO 527-2/1A/50 | >50 % |
| Tensile creep modulus | 1hr | ISO 899-1 | 460 MPa |
| Tensile creep modulus | 1000hr | ISO 899-1 | 230 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 无断裂 |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 无断裂 |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Charpy Notched Impact Strength | | ISO 1152-2 | 240 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| dielectric constant | 100Hz | IEC 60250 | 2.00 |
| dielectric constant | 1MHz | IEC 60250 | 2.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 3.9E-04 |
| Dissipation Factor | 1MHz | IEC 60250 | 1E-03 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Surface Resistivity | -- | ASTM D257 | >1.0E+13 ohms |
| Surface Resistivity | -- | IEC 60093 | >1.0E+12 ohms |
| Volume resistivity | -- | ASTM D257 | >1.0E+15 ohms·cm |
| Volume resistivity | -- | IEC 60093 | >1.0E+14 ohms·cm |
| dielectric strength | | IEC 60243-1 | 45 kV/mm |
| dielectric constant | 1MHz | ASTM D150 | 3.00 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 65.0 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 38.0 °C |
| vicat | | ASTMD1525 | 80.0 °C |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 2E-04 cm/cm/°C |
| specific heat | 23°C | 内部方法 | 1840 J/kg/°C |
| thermal conductivity | 23°C | 内部方法 | 0.41 W/m/K |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.