PC RAMLLOY PZF101
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.20 g/cm³ | |
| ISO 1183 | 1.20 g/cm³ | ||
| melt mass-flow rate | 250°C/5.0kg | ASTM D1238 | 18 g/10min |
| 250°C/5.0kg | ISO 1133 | 18 g/10min | |
| Shrinkage rate | MD | ASTM D955 | 3E-03 % |
| ISO 2577 | 3E-03 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 1800 MPa | |
| ISO 527-2 | 1800 MPa | ||
| tensile strength | Yield | ASTM D638 | 50.0 MPa |
| Yield | ISO 527-2 | 50.0 MPa | |
| elongation | Break | ASTM D638 | 140 % |
| Tensile strain | Break | ISO 527-2 | 140 % |
| Flexural modulus | ASTM D790 | 1700 MPa | |
| ISO 178 | 1700 MPa | ||
| bending strength | ASTM D790 | 75.0 MPa | |
| ISO 178 | 75.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 550 J/m |
| 23°C | ASTM D256 | 750 J/m | |
| -30°C | ISO 180 | 55 kJ/m² | |
| 23°C | ISO 180 | 65 kJ/m² |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 115 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 115 °C | |
| 1.8MPa,未退火，HDT | ASTM D648 | 90.0 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 90.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.