impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of cantilever beam gap	23°C	ISO 180/1A	80	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-40°C	ISO 180/1A	40	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	75	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	26	kJ/m²
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Bending modulus	160°C	ISO 178	350	Mpa
	Bending modulus	120°C	ISO 178	400	Mpa
	Bending modulus	Bending modulus	--	ISO 178	1800	Mpa
Nominal tensile fracture strain	160°C	ISO 527-2	> 50	%
	Nominal tensile fracture strain	120°C	ISO 527-2	> 50	%
	Nominal tensile fracture strain	Nominal tensile fracture strain	--	ISO 527-2	> 50	%
tensile strength	Yield, 160°C	ISO 527-2	30.0	Mpa
	tensile strength	Yield, 120°C	ISO 527-2	35.0	Mpa
	tensile strength	tensile strength	Yield	ISO 527-2	60.0	Mpa
Tensile modulus	160°C	ISO 527-2	350	Mpa
	Tensile modulus	120°C	ISO 527-2	400	Mpa
	Tensile modulus	Tensile modulus	--	ISO 527-2	1850	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Melting temperature		ISO 11357-3	295	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.6E-4	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.8E-4	cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	90.0	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	200	°C
Thermal Index - 5000 hr		IEC 60216	135	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	3.0	%
Shrinkage rate	Flow	ISO 294-4	2.0	%
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	2.0	%
density		ISO 1183	1.10	g/cm³
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Dielectric strength		IEC 60243-1	25	KV/mm
Relative permittivity	100 Hz	IEC 60250	3.60
Relative permittivity	Relative permittivity	1 MHz	IEC 60250	3.20
Compared to the anti leakage trace index		IEC 60112	PLC 1