impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	-40°C	ISO 179	12	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	15	kJ/m²
Impact strength of simply supported beam without notch	-40°C	ISO 179	85	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	90	kJ/m²
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength	-40°C	ISO 527-2	280	Mpa
	tensile strength	23°C	ISO 527-2	220	Mpa
	tensile strength	tensile strength	80°C	ISO 527-2	140	Mpa
Tensile strain	Break, -40°C	ISO 527-2	2.5	%
	Tensile strain	Break, 23°C	ISO 527-2	3.0	%
	Tensile strain	Tensile strain	Break, 80°C	ISO 527-2	5.5	%
Bending modulus	-40°C	ISO 178	15500	Mpa
	Bending modulus	23°C	ISO 178	13800	Mpa
	Bending modulus	Bending modulus	80°C	ISO 178	8600	Mpa
bending strength	-40°C	ISO 178	380	Mpa
	bending strength	23°C	ISO 178	345	Mpa
	bending strength	bending strength	80°C	ISO 178	230	Mpa
Compressive stress	-40°C	ISO 604	265	Mpa
	Compressive stress	23°C	ISO 604	195	Mpa
	Compressive stress	Compressive stress	80°C	ISO 604	120	Mpa
shear strength	23°C	ASTM D732	105	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	263	°C
Melting temperature		DSC	265	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.0E-5 - 3.0E-5	cm/cm/°C
specific heat			1500	J/kg/°C
thermal conductivity			0.42	W/m/K
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density	23°C	ISO 1183	1.50	g/cm³
Shrinkage rate	横向Flow : 3.00 mm	Internal Method	0.50 - 0.80	%
Shrinkage rate	Shrinkage rate	Flow : 3.00 mm	Internal Method	0.20 - 0.40	%
Water absorption rate	24 hr, 23°C	ISO 62	0.40	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	4.8	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Volume resistivity		IEC 60093	1.0E+13	ohms·cm
Dielectric strength		IEC 60243-1	19	KV/mm
Dielectric constant	23°C, 50 Hz	IEC 60250	4.70
	Dielectric constant	23°C, 1 kHz	IEC 60250	4.50
	Dielectric constant	Dielectric constant	23°C, 1 MHz	IEC 60250	4.10
Dissipation factor	23°C, 50 Hz	IEC 60250	0.020
	Dissipation factor	23°C, 1 kHz	IEC 60250	0.020
	Dissipation factor	Dissipation factor	23°C, 1 MHz	IEC 60250	0.020
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	M -Sale, 23°C	ISO 2039-2	103
Rockwell hardness	Rockwell hardness	R -Sale, 23°C	ISO 2039-2	121

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.