229
- ویژگی‌ها:مقاومت در برابر مواد شیمیجریان بالاتقویت فیبر شیشه ایمقاومت بالا
- کاربردها:قطعات خارجی خودرو
مقایسه
مشاهده قیمتهابرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melt mass-flow rate | 250°C/5.0 kg | ASTM D1238 | 15 g/10 min |
| Melt volume flow rate | 265°C/5.0 kg | ISO 1133 | 27.0 cm3/10min |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.40 - 0.60 % |
| 横向流动 : 3.20 mm | 内部方法 | 0.40 - 0.60 % | |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.50 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.15 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | --1 | ASTM D638 | 5310 Mpa |
| -- | ISO 527-2/1 | 4800 Mpa | |
| tensile strength | 屈服2 | ASTM D638 | 84.0 Mpa |
| 屈服 | ISO 527-2/5 | 84.0 Mpa | |
| 断裂2 | ASTM D638 | 84.0 Mpa | |
| 断裂 | ISO 527-2/5 | 84.0 Mpa | |
| elongation | 屈服2 | ASTM D638 | 3.0 % |
| 屈服 | ISO 527-2/5 | 3.0 % | |
| 断裂2 | ASTM D638 | 3.0 % | |
| 断裂 | ISO 527-2/5 | 3.0 % | |
| Flexural modulus | 50.0 mm 跨距3 | ASTM D790 | 3910 Mpa |
| --4 | ISO 178 | 4010 Mpa | |
| bending strength | --4,5 | ISO 178 | 133 Mpa |
| 屈服, 50.0 mm 跨距3 | ASTM D790 | 131 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Dart impact | -30°C, Energy at Peak | ASTM D3763 | 3.00 J |
| -30°C, Total Energy | ASTM D3763 | 3.00 J | |
| -20°C, Energy at Peak | ASTM D3763 | 4.00 J | |
| 23°C, Total Energy | ASTM D3763 | 8.00 J |
| injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| drying temperature | 110 °C | ||
| drying time | 4.0 to 6.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 50 to 80 % | ||
| Temperature at the rear of the barrel | 250 to 270 °C | ||
| Temperature in the middle of the barrel | 255 to 275 °C | ||
| Temperature at the front of the material cylinder | 260 to 280 °C | ||
| Spray nozzle temperature | 255 to 275 °C | ||
| Processing (melt) temperature | 260 to 280 °C | ||
| Temperature | 65 to 95 °C | ||
| Back pressure | 0.300 to 0.600 Mpa | ||
| screw speed | 50 to 80 rpm | ||
| Exhaust hole depth | 0.013 to 0.020 mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 125 °C |
| 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 116 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距7，HDT | ISO 75-2/Af | 101 °C | |
| vicat | -- | ASTM D15258 | 121 °C |
| -- | ISO 306/B50 | 135 °C | |
| -- | ISO 306/B120 | 130 °C | |
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 3.9E-5 cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 7.6E-5 cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 7.6E-5 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.