PEEK AVASPIRE® AV-750 SOLVAY USA

مقایسه مشاهده قیمت‌ها

برگه داده فنی

Filling analysis	شرایط آزمون	روش آزمون	نتیجه آزمون
Melt viscosity	400°C, 1000 sec^-1	ASTM D3835	450 Pa·s

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Suspended wall beam without notch impact strength	--	ASTM D4812	590 J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	--	ISO 180	41 kJ/m²

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	0.8 mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating	1.6 mm	UL 94	V-0

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	--5	ASTM D638	15100 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1A/1	16700 Mpa
tensile strength	Yield, 5.00 mm	ISO 527-2/1A/5	188 Mpa
tensile strength	tensile strength	--6	ASTM D638	191 Mpa
elongation	Break5	ASTM D638	1.8 %
elongation	elongation	Break	ISO 527-2/1A/5	1.8 %
Bending modulus	--	ASTM D790	14800 Mpa
Bending modulus	Bending modulus	--	ISO 178	15400 Mpa
bending strength	23°C	ASTM D790	253 Mpa
	bending strength	250°C	ASTM D790	54.0 Mpa
	bending strength	bending strength	--	ISO 178	250 Mpa
compressive strength		ASTM D695	182 Mpa
shear strength		ASTM D732	89.0 Mpa

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			150 to 175 °C
drying time			2.5 to 4.0 hr
Processing (melt) temperature			370 to 395 °C
Mold temperature			175 to 210 °C
Back pressure			0.138 to 0.345 Mpa
Screw speed			75 rpm
Screw compression ratio			2.0:1.0

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	1.8 MPa, Annealed	ASTM D648	285 °C
Glass transition temperature		ASTM D3418	150 °C
Melting temperature		ASTM D3418	345 °C
Linear coefficient of thermal expansion	-50 to 50°C，Flow	ASTM E831	1.5E-5 cm/cm/°C
specific heat	50°C	DSC	1260 J/kg/°C
specific heat	specific heat	200°C	DSC	1620 J/kg/°C
thermal conductivity		ASTM E1530	0.31 W/m/K

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	380°C/2.16 kg	ASTM D1238	7.0 g/10 min
Shrinkage rate	Flow : 3.18 mm	ASTM D955	0.10 - 0.30 %
Shrinkage rate	Shrinkage rate	Across FlowFlow : 3.18 mm	ASTM D955	1.2 - 1.4 %
Water absorption rate	24 hr	ASTM D570	0.10 %

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface resistivity		ASTM D257	> 1.9E+17 ohms
Volume resistivity		ASTM D257	1.8E+17 ohms·cm
Dielectric strength		ASTM D149	19 KV/mm
Dielectric constant	60 Hz	ASTM D150	3.68
	Dielectric constant	1 kHz	ASTM D150	3.69
	Dielectric constant	Dielectric constant	1 MHz	ASTM D150	3.66
Dissipation factor	60 Hz	ASTM D150	2.0E-3
	Dissipation factor	1 kHz	ASTM D150	1.0E-3
	Dissipation factor	Dissipation factor	1 MHz	ASTM D150	3.0E-3

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	M-Scale	ASTM D785	105