TPU-Ester Generic TPU-Polyester Generic

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

elastomer	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength	Break,23°C	ASTM D412	23.7to64.1	MPa
	tensile strength	Break,23°C	ISO 37	19.0to55.0	MPa
	tensile strength	tensile strength	23°C	ASTM D412	25.0to40.3	MPa
elongation	Yield	ASTM D412	390to800	%
	elongation	Break,23°C	ASTM D412	340to750	%
	elongation	elongation	Break,23°C	ISO 37	300to950	%
tear strength	23°C	ASTM D624	33.3to206	kN/m
	tear strength	Split	ASTM D470	34	kN/m
	tear strength	tear strength	23°C	ISO 34-1	32to190	kN/m
Permanent compression deformation	--	ASTM D395	18to76	%
Permanent compression deformation	Permanent compression deformation	23°C	ISO 815	19to30	%
Shore hardness		ASTM D2632	25to45	%
tensile strength	Yield,23°C	ISO 37	24.6to55.0	MPa
	tensile strength	20%Strain,23°C	ISO 37	0.500to8.06	MPa
		tensile strength	50%Strain,23°C	ASTM D412	1.68to15.3	MPa
			tensile strength	100%Strain,23°C	ASTM D412	1.62to19.1	MPa
				tensile strength	100%Strain,23°C	ISO 37	1.00to11.2	MPa
					tensile strength	300%Strain,23°C	ASTM D412	3.00to29.7	MPa
						tensile strength	300%Strain,23°C	ISO 37	1.50to35.2	MPa
						tensile strength	tensile strength	Yield,23°C	ASTM D412	23.7to55.7	MPa
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Bending modulus	23°C	ASTM D790	13.4to403	MPa
Bending modulus	Bending modulus	23°C	ISO 178	13.4to367	MPa
Taber abraser	23°C	ASTM D1044	8.80to71.2	mg
Tensile modulus	23°C	ISO 527-2	140to730	MPa
tensile strength	Break,23°C	ISO 527-2	27.2to63.5	MPa
	tensile strength	23°C	ASTM D638	1.00to45.9	MPa
	tensile strength	tensile strength	23°C	ISO 527-2	0.500to22.5	MPa
elongation	Break,23°C	ASTM D638	10to740	%
elongation	elongation	Break,23°C	ISO 527-2	320to940	%
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Melting temperature	--		68.0to215	°C
Melting temperature	Melting temperature	--	DSC	106to227	°C
Linear coefficient of thermal expansion	MD	ASTM D696	9.3E-5到2.0E-4	cm/cm/°C
Brittle temperature		ASTM D746	-67.8--12.8	°C
Glass transition temperature	--	DSC	-45.1--14.5	°C
Vicat softening temperature	--	ASTM D1525	57.8to160	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306	38.9to155	°C
Glass transition temperature	--	ASTME1356	-50.0-0.00	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density	--	ISO 11831	1210	kg/m³
density	density	--	ASTM D1505	0.340to1.22	g/cm³
Melt Volume Flow Rate (MVR)	190°C/21.6kg	ISO 1133	34.1to76.6	cm³/10min
Shrinkage rate	MD:23°C	ASTM D955	0.39to1.1	%
	Shrinkage rate	TD:23°C	ASTM D955	0.79to0.82	%
	Shrinkage rate	Shrinkage rate	23°C	ISO 294-4	0.76to0.82	%
Water absorption rate	23°C,24hr	ASTM D570	0.30to0.40	%
Solution viscosity		ASTM D445	14850to35000	mPa·s
density	--	ASTM D792	1.14to1.23	g/cm³
density	density	23°C	ISO 1183	1.15to1.25	g/cm³
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Surface resistivity		ASTM D257	1.0E+6到2.5E+10	ohms
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shore hardness	23°C	ASTM D2240	34to96
	Shore hardness	23°C	ISO 868	30to98
		Shore hardness	ShoreA,3sec	ISO 8681	80to98
		Shore hardness	Shore hardness	ShoreD,15sec	ISO 8681	32to60
aging	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Change rate of tensile strength in air	23°C	ASTMD471	-29-7.0	%
Volume change	23°C	ASTM D471	0.60to24	%

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.