HIPS 9200
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D-792 | 1.04 g/cm3 | |
| Apparent density | ASTM D-792 | 0.59-0.64 g/cm3 | |
| melt mass-flow rate | 200℃/5.0kg | ASTM D-1238 | 2.5 g/10min |
| Shrinkage rate | MD，23℃ | ASTM D-955 | 0.40-0.70 % |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| gloss | 60° | ASTM D-523 | 10 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Rockwell hardness | ASTM D-785 | 42 L Scale | |
| Tensile modulus | 23℃ | ASTM D-638 | 1690 MPa |
| tensile strength | 23℃，屈服 | ASTM D-638 | 19.0 MPa |
| elongation at break | 23℃ | ASTM D-638 | 40 % |
| Flexural modulus | 23℃ | ASTM D-790 | 1660 MPa |
| bending strength | 23℃ | ASTM D-790 | 39.0 MPa |
| Impact strength of cantilever beam gap | 23℃， 3.18mm | ASTM D-256 | 123 J/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| dielectric strength | 23℃，3.18mm | ASTM D-149 | 16 kV/mm |
| dielectric constant | 23℃， 1MHz | ASTM D-150 | 2.50 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa，退火，HDT | ASTM D-648 | 86.0 ℃ |
| vicat | ASTM D-1525 | 102 ℃ | |
| Linear coefficient of thermal expansion | Flow | ASTM D-696 | 0.000090 ℃ |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.