برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20-0.40 % |
| Water absorption rate | 24hr | ASTM D570 | 0.12 % |
| Water absorption rate | 平衡,23°C | ASTM D570 | 0.31 % |
| Outdoor applicability | | UL 746C | f1 |
| Specific volume | | ASTM D792 | 0.802 cm³/g |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M计秤 | ASTM D785 | 85 |
| Rockwell hardness | R计秤 | ASTM D785 | 124 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| UL flame retardant rating | 3.0mm | UL 94 | 5VA |
| Limiting Oxygen Index | | ASTM D2863 | 36 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 屈服 | ASTM D638 | 66.2 Mpa |
| tensile strength | 断裂 | ASTM D638 | 55.2 Mpa |
| elongation | 屈服 | ASTM D638 | 8.0 % |
| elongation | 断裂 | ASTM D638 | 15 % |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 3450 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 103 Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 11.0 mg |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Dart impact | 23°C | ASTM D3029 | 102 J |
| Impact strength of cantilever beam gap | | ASTM D1822 | 158 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | >1.0E+17 ohms·cm |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 18 KV/mm |
| dielectric constant | 50Hz | ASTM D150 | 3.10 |
| dielectric constant | 60Hz | ASTM D150 | 3.10 |
| dielectric constant | 1MHz | ASTM D150 | 3.05 |
| Dissipation Factor | 50Hz | ASTM D150 | 8E-04 |
| Dissipation Factor | 60Hz | ASTM D150 | 8E-04 |
| Dissipation Factor | 1MHz | ASTM D150 | 7.5E-03 |
| arc resistance | | ASTM D495 | PLC7 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 1 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 3.2E-05 cm/cm/°C |
| specific heat | | ASTMC351 | 1210 J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.20 W/m/K |
| RTI Elec | | UL 746 | 120 °C |
| RTI Imp | | UL 746 | 110 °C |
| RTI Str | | UL 746 | 125 °C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 146 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 142 °C |
| vicat | | ASTM D15255 | 154 °C |