برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D-792 | 0.935 g/cm³ |
| density | | ISO 1183/A | 0.935 g/cm³ |
| Content of comonomer | | 内部方法 | 6.5 % |
| melt mass-flow rate | 190°C/2.16kg | ASTMD1238 | 2.6 g/10min |
| density | | ASTMD792 | 0.935 g/cm³ |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| gloss | 45°，50.8um | ASTM D-2457 | 76 |
| Haze ratio | 50.8um | ASTM D-1003 | 3.7 % |
| Haze ratio | 50.8um | ISO 14782 | 3.7 % |
| gloss | 45°,50.8µm | ASTM D2457 | 76 |
| Haze ratio | 50.8µm | ISO 14782 | 3.7 % |
| Haze ratio | 50.8µm | ASTM D1003 | 3.7 % |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 190℃/2.16kg | ASTM D-1238 | 2.6 g/10min |
| melt mass-flow rate | 190℃/2.16kg | ISO 1133 | 2.6 g/10min |
| Monomer content | | Internal Method | 6.5 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 屈服,Compression Molded | ASTM D-638 | 10 MPa |
| tensile strength | 屈服,Compression Molded | ISO 527-2/508 | 10 MPa |
| tensile strength | Compression Molded，断裂 | ASTM D-638 | 20.1 MPa |
| tensile strength | 50.8um，TD,断裂 | ISO 527-3 | 31.8 MPa |
| tensile strength | 50.8um，MD,断裂 | ISO 527-3 | 31.8 MPa |
| elongation at break | 50.8um，TD | ASTM D-882 | 510 % |
| elongation at break | 50.8um，MD | ASTM D-882 | 460 % |
| elongation at break | 50.8um，MD | ISO 527-3 | 460 % |
| elongation at break | 50.8um，TD | ISO 527-3 | 510 % |
| Dart impact | 50.8um | ASTM D-1709B | 410 g |
| Dart impact | 50.8um | ISO 7765-1/B | 410 g |
| Elmendorf tear strength | 50.8um，MD | ASTM D-1922 | 270 g |
| Elmendorf tear strength | 50.8um，TD | ASTM D-1922 | 390 g |
| tensile strength | Compression Molded，断裂 | ISO 527-2/508 | 20.1 MPa |
| elongation at break | Compression Molded | ASTM D-638 | 640 % |
| elongation at break | Compression Molded | ISO 527-2/508 | 640 % |
| tensile strength | 50.8um，屈服,MD | ASTM D-882 | 11.3 MPa |
| tensile strength | 50.8um，屈服,TD | ASTM D-882 | 11.1 MPa |
| tensile strength | 50.8um，屈服,MD | ISO 527-3 | 11.3 MPa |
| tensile strength | 50.8um，屈服,TD | ISO 527-3 | 11.5 MPa |
| tensile strength | 50.8um，TD,断裂 | ASTM D-882 | 31.8 MPa |
| tensile strength | 50.8um，MD,断裂 | ASTM D-882 | 31.8 MPa |
| Elmendorf tear strength | 50.8um，MD | ISO 6383-2 | 1200 N |
| Elmendorf tear strength | 50.8um，TD | ISO 6383-2 | 1700 N |
| elongation | 断裂,模压成型 | ISO 527-2/508 | 640 % |
| elongation | 断裂,模压成型4 | ASTM D638 | 640 % |
| tensile strength | 断裂,模压成型 | ISO 527-2/508 | 20.1 Mpa |
| tensile strength | 断裂,模压成型4 | ASTM D638 | 20.1 Mpa |
| tensile strength | 屈服,模压成型 | ISO 527-2/508 | 10.0 Mpa |
| tensile strength | 屈服,模压成型4 | ASTM D638 | 10.0 Mpa |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Elmendorf tear strength | TD:51µm | ASTM D1922 | 390 g |
| Elmendorf tear strength | MD:51µm | ISO 6383-2 | 1200 N |
| Elmendorf tear strength | TD:51µm | ISO 6383-2 | 1700 N |
| tensile strength | MD:屈服,51µm | ASTM D882 | 11.3 Mpa |
| tensile strength | TD:屈服,51µm | ASTM D882 | 11.1 Mpa |
| tensile strength | MD:屈服,51µm | ISO 527-3 | 11.3 Mpa |
| tensile strength | TD:屈服,51µm | ISO 527-3 | 11.5 Mpa |
| tensile strength | MD:断裂,51µm | ASTMD882 | 31.8 Mpa |
| tensile strength | TD:断裂,51µm | ASTMD882 | 31.8 Mpa |
| elongation | MD:断裂,51µm | ASTMD882 | 460 % |
| elongation | TD:断裂,51µm | ASTMD882 | 510 % |
| Dart impact | 51µm | ASTMD1709B | 410 g |
| Elmendorf tear strength | MD:51µm | ASTM D1922 | 270 g |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| vicat | | ASTM D-1525 | 88.9 ℃ |
| vicat | | ISO 306 | 88.9 ℃ |
| melting temperature | DSC | | 103 ℃ |
| vicat | | ASTMD1525 | 88.9 °C |
| melting temperature | | 内部方法 | 103 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.