PC 301-9 Trinseo

کاربردها:
Household goods
electrical and electronic application fields
electrical appliances
casings
packaging
business equipment
lighting applications
مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ISO 1183/A	1.20 g/cm³
melt mass-flow rate	300°C/1.2kg	ASTM D1238	9.0 g/10min
melt mass-flow rate	melt mass-flow rate	300°C/1.2kg	ISO 1133	9.0 g/10min
Shrinkage rate	MD	ASTM D955	0.50to0.70 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.50to0.70 %
Water absorption rate	23°C,24hr	ASTM D570	0.15 %
	Water absorption rate	23°C,24hr	ISO 62	0.15 %
		Water absorption rate	平衡,23°C,50%RH	ASTM D570	0.32 %
		Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.32 %
density		ASTM D792	1.20 g/cm³

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	M计秤	ASTM D785	73
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	118

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
refractive index		ASTM D542	1.586
refractive index	refractive index		ISO 489	1.586
transmissivity		ASTM D1003	89.0 %
Haze ratio		ASTM D1003	1.0 %

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	1.6mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	HB
Limiting Oxygen Index		ISO 4589-2	26 %
Average degree of combustion		ASTM D635	3 cm

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ASTM D638	2410 MPa
Flexural modulus		ISO 178	2400 MPa
bending strength		ASTM D790	96.5 MPa
bending strength	bending strength		ISO 178	97.0 MPa
Taber abraser		ASTM D1044	45 %
tensile strength	Yield	ASTM D638	60.0 MPa
	tensile strength	Yield	ISO 527-2/50	60.0 MPa
		tensile strength	Break	ASTM D638	71.0 MPa
		tensile strength	tensile strength	Break	ISO 527-2/50	71.0 MPa
elongation	Yield	ASTM D638	6.0 %
Tensile strain	Yield	ISO 527-2/50	6.0 %
elongation	Break	ASTM D638	150 %
Tensile strain	Break	ISO 527-2/50	150 %
Tensile modulus		ISO 527-2/50	2300 MPa
Flexural modulus		ASTM D790	2410 MPa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	23°C	ISO 179/1eA	35 kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256	910 J/m
	Impact strength of cantilever beam gap	23°C	ISO 180/A	90 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	NoBreak
Suspended wall beam without notch impact strength	23°C	ISO 180	NoBreak
InstrumentedDartImpact	23°C,TotalEnergy	ASTM D3763	87.0 J

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Compared to the Leakage Tracking Index (CTI)	2.00mm,SolutionA	IEC 60112	PLC 2
dielectric strength		IEC 60243-1	17 kV/mm
dielectric constant	60Hz	ASTM D150	3.00
dielectric constant	dielectric constant	1MHz	ASTM D150	3.00
Dissipation Factor	50Hz	ASTM D150	1E-03
Dissipation Factor	Dissipation Factor	1MHz	ASTM D150	2E-03
Volume resistivity		ASTM D257	2E+17 ohms·cm
dielectric strength		ASTM D149	17 kV/mm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,退火，HDT	ASTM D648	144 °C
	Heat distortion temperature	0.45MPa,退火，HDT	ISO 75-2/B	144 °C
		Heat distortion temperature	1.8MPa,未退火，HDT	ASTM D648	128 °C
			Heat distortion temperature	1.8MPa,未退火，HDT	ISO 75-2/A	125 °C
				Heat distortion temperature	1.8MPa,退火，HDT	ASTM D648	141 °C
				Heat distortion temperature	Heat distortion temperature	1.8MPa,退火，HDT	ISO 75-2/A	141 °C
vicat		ASTM D15256	149 °C
vicat	vicat		ISO 306/B50	149 °C
Ball pressure temperature		IEC 60335-1	125 °C
Linear coefficient of thermal expansion	MD：-40到82°C	ASTM D696	6.8E-05 cm/cm/°C

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.