PA66/6 BKV 215 H2.0 DUS035 900051 LANXESS GERMANY

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	80 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	70 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	65 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	20 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	60 kJ/m²
Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	4.00 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	10.0 J
Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	750 N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	1500 N
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	20 kJ/m²

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	23°C	ISO 527-2/1	4300 MPa
tensile strength	Break,23°C	ISO 527-2/5	85.0 MPa
Tensile strain	Break,23°C	ISO 527-2/5	4.5 %
Bending modulus	23°C	ISO 178/A	4000 MPa
bending strength	3.5%Strain,23°C	ISO 178/A	120 MPa
bending strength	bending strength	23°C4	ISO 178/A	135 MPa
Bending strain	23°C	ISO 178/A	5.5 %

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	175 °C
Vicat softening temperature		ISO 306/B120	200 °C
Melting temperature		ISO 11357-3	214 °C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	4E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	1.5E-04 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	200 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density	23°C	ISO 1183	1.17 g/cm³
Apparent density		ISO 60	0.60 g/cm³
Shrinkage rate	TD:280°C,2.00mm2	ISO 2577	0.80 %
	Shrinkage rate	TD:120°C,4hr,2.00mm3	ISO 2577	0.10 %
		Shrinkage rate	MD:280°C,2.00mm2	ISO 2577	0.50 %
		Shrinkage rate	Shrinkage rate	MD:120°C,4hr,2.00mm3	ISO 2577	0.10 %
Water absorption rate	Saturation,23°C	ISO 62	7.0 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.0 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Ball Pressure Test		ISO 2039-1	120 MPa

Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون
ISO Shortcut		ISO 1874	PA6/66-HI.GHR.14-040.GF15

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.