| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 0.908 g/cm³ | |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 1.5 % |
| Water absorption rate | 24hr | ASTM D570 | 5E-03 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | Yield | ASTM D638 | 34.5 MPa |
| elongation | Yield | ASTM D638 | 10 % |
| bending strength | Yield | ASTM D790 | 48.3 MPa |
| compressive strength | ASTM D695 | 46.9 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 21 J/m |
| Suspended wall beam without notch impact strength | 23°C,6.35mm | ASTM D256 | 850 J/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| dielectric strength | ASTM D149 | 26 kV/mm | |
| dielectric constant | ASTM D150 | 2.25 | |
| Dissipation Factor | ASTM D150 | 2E-04 | |
| Volume resistivity | ASTM D257 | 1E+17 ohms·cm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ASTM D648 | 118 °C |
| 1.8MPa,未退火，HDT | ASTM D648 | 98.9 °C | |
| 线性热膨胀系数 | MD | ASTM D696 | 6.8E-05 cm/cm/°C |
| thermal conductivity | ASTMC177 | 0.12 W/m/K |