| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.30 g/cm³ |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 22.0 cm³/10min |
| Shrinkage rate | TD | ISO 2577 | 1.8 % |
| Shrinkage rate | MD | ISO 2577 | 1.8 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.25 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.50 % |
| Viscosity value | 降低的粘度 | ISO 1628 | 140.0 ml/g |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| ball-indentation hardness | | ISO 2039-1 | 135 MPa |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.8mm | 内部方法 | HB |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 750 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| bending strength | 3.5%应变 | ISO 178 | 75.0 MPa |
| Bending Strain | | ISO 178 | 6.0 % |
| Tensile modulus | | ISO 527-2/1 | 2600 MPa |
| tensile strength | Yield | ISO 527-2/50 | 60.0 MPa |
| Tensile strain | Yield | ISO 527-2/50 | 6.0 % |
| Nominal tensile fracture strain | | ISO 527-2/50 | >50 % |
| Flexural modulus | | ISO 178 | 2200 MPa |
| bending strength | -- | ISO 178 | 80.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 5.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 6.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 200 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 1E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | 1.00mm | IEC 60243-1 | 26 kV/mm |
| relative permittivity | 100Hz | IEC 60250 | 3.40 |
| relative permittivity | 1MHz | IEC 60250 | 3.20 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD:23到80°C | ISO 11359-2 | 1.3E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | TD:23到80°C | ISO 11359-2 | 1.3E-04 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 165 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 60.0 °C |
| vicat | | ISO 306/B50 | 180 °C |
| melting temperature | | ISO 11357-3 | 223 °C |