MF MELOPAS® MF 152 RASCHIG GmbH

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	Compression Molded	ISO 179/1eA	1.2to1.8 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Injection	ISO 179/1eA	1.4to2.0 kJ/m²
Impact strength of simply supported beam without notch	Compression Molded	ISO 179/1eU	5.0to9.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Injection	ISO 179/1eU	7.0to12 kJ/m²

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	1.5mm	UL 94	V-0
Burning wire flammability index		IEC 60695-2-12	960 °C
Hot filament ignition temperature		IEC 60695-2-13	900 °C

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	Compression Molded	ISO 527-2	5000to8000 MPa
Tensile modulus	Tensile modulus	Injection	ISO 527-2	5000to8000 MPa
tensile strength	CompressionMolded	ISO 527-2	45.0to65.0 MPa
tensile strength	tensile strength	Injection	ISO 527-2	50.0to90.0 MPa
Bending modulus	Compression Molded	ISO 178	8000to9000 MPa
Bending modulus	Bending modulus	Injection	ISO 178	8000to9000 MPa
bending strength	Compression Molded	ISO 178	80.0to110 MPa
bending strength	bending strength	Injection	ISO 178	90.0to130 MPa
Compressive stress		ISO 604	200to250 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	110to130 °C
Linear coefficient of thermal expansion	MD：50to100°C	ISO 11359-2	1.5E-5到3.5E-5 cm/cm/°C
thermal conductivity		ASTME1461	0.40to0.50 W/m/K
Maximum operating temperature	<50h	IEC 60216	160 °C
Maximum operating temperature	Maximum operating temperature	20,000h	IEC 60216	135 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	155to180 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Apparent density		ISO 60	0.55to0.75 g/cm³
Shrinkage rate	MD：--2	ISO 2577	0.80to1.3 %
Shrinkage rate	Shrinkage rate	MD：--3	ISO 2577	0.50to1.0 %
Water absorption rate	23°C,24hr	ISO 62	<2.0 %
Shrinkage rate		ISO 2577	1.0to1.5 %
density		ISO 1183	1.50to1.70 g/cm³

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface resistivity		IEC 60093	1.0E+10到1.0E+11 ohms
Volume resistivity		IEC 60093	1.0E+11到1.0E+12 ohms·cm
Dielectric strength		IEC 60243-1	15to20 kV/mm
Relative permittivity	100Hz	IEC 60250	11.016.0
Relative permittivity	Relative permittivity	1MHz	IEC 60250	7.009.00
Compared to the anti leakage trace index		IEC 60112	PLC 0
Dissipation factor	100Hz	IEC 60250	0.30to0.50
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.030to0.050
Arc resistance		ASTM D495	PLC 5

Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون
Compression molding pressure			>20.0 MPa
Compression molding temperature			160to180 °C

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.