برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D-792 | 1.05 |
| Shrinkage rate | flow,0.125" | ASTM D-955 | 4-6 in/inE-3 |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 230℃,3.8kg | ASTM D-1238 | 4.4 g/10min |
| melt mass-flow rate | 220℃,10kg | ISO 1133 | 16 g/10min |
| melt viscosity | 240℃,1000sec-1 | ASTM D-3825 | 2550 poise |
| Other performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rated HB value | 测试厚度 | UL 94 | 0.060 inch |
| Compared to the Leakage Tracking Index (CTI) | | UL 746A | PLC 5 |
| Hot metal wire test | | UL 746A | PLC_3 |
| Tungsten resistance | | ASTM D-495 | PLC_6 |
| High Ampere Arc Igniter, Surface | | UL 746A | PLC_3 |
| UL file number | | | E121562 |
| High voltage bow orbit rate | | UL 746A | PLC_3 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Flexural modulus | 0.05in/min,2"span | ASTM D-790 | 355000 psi |
| tensile strength | 屈服,类型1,0.2in/min | ASTM D-638 | 6150 psi |
| elongation at break | 类型1,0.2in/min | ASTM D-638 | 30.0 % |
| tensile strength | 类型1,0.2in/min，断裂 | ASTM D-638 | 4900 psi |
| Impact strength of cantilever beam gap | 73F | ASTM D-256 | 6.5 ft-lb/in |
| elongation at yield | 类型1,0.2in/min | ASTM D-638 | 2.2 % |
| Tensile modulus | 0.2in/min | ASTM D-638 | 345000 psi |
| bending strength | 0.05in/min,2"span，屈服 | ASTM D-790 | 10600 psi |
| Instrumented impact | 73F | ASTM D-3763 | 304 in-lbs |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | xflow,-40Fto100F | ASTM E-831 | 4.1E-05 1/F |
| Linear coefficient of thermal expansion | flow,-40Fto100F | ASTM E-831 | 4.3E-05 1/F |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 264PSi, 0.250",未退火，HDT | ASTM D-648 | 185 deg F |
| vicat | | ASTM D-1525 | 214 deg F |
| Heat index | 电性能 | UL 746B | 60 deg C |
| Heat index | 机械冲击性能 | UL 746B | 60 deg C |
| Heat index | 非机械冲击性能 | UL 746B | 60 deg C |
| Heat distortion temperature | 66PSi, 0.125",未退火，HDT | ASTM D-648 | 210 deg F |