PP Polifor® ECO 30 CA/40 GRIGIO Y1 SO.F.TER ITALY

ویژگی‌ها:
Filler mineral filler 40% filler by weight
مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23°C	ASTM D256	23 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	23 J/m

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	1.6mm	UL 94	HB
	UL flame retardant rating	3.2mm	UL 94	HB
		UL flame retardant rating	1.6mm	UL 94	HB
		UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	HB

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Yield	ASTM D638	20.0 MPa
elongation	Break	ASTM D638	30 %
tensile strength	Yield	ASTM D638	20.0 MPa
elongation	Break	ASTM D638	30 %
Bending modulus		ASTM D790	1900 MPa
Bending modulus	Bending modulus		ASTM D790	1900 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Vicat softening temperature		ASTM D15252	93.0 °C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	57.0 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	57.0 °C
Vicat softening temperature		ASTM D15252	93.0 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.24 g/cm³
melt mass-flow rate	230°C/2.16kg	ASTM D1238	19 g/10min
Shrinkage rate		Internal Method	1.3 %
density		ASTM D792	1.24 g/cm³
melt mass-flow rate	230°C/2.16kg	ASTM D1238	19 g/10min
Shrinkage rate		Internal Method	1.3 %