برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | | ASTM D1238 | 10 g/10min |
| Shrinkage rate | flow, 3.2 | Internal | 0.4-0.8 |
| Shrinkage rate | xflow, 3.2 | Internal | 0.4-0.6 |
| Water absorption rate | flow, 3.2 | ASTM D570 | 0.4 |
| Water absorption rate | 24 hours | ASTM D570 | 0.1 |
| Thermal Properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| vicat | Rate B/50 | ASTM D1525 | 85 °C |
| RTI Imp | | UL 746B | 85 °C |
| RTI Elec | | UL 746B | 85 °C |
| RTI Imp | | UL 746B | 85 °C |
| Linear coefficient of thermal expansion | -30°C to 3，流动 | ASTM E831 | 72 E-6/°C |
| Linear coefficient of thermal expansion | -30°C to 3，横向 | ASTM E831 | 72 E-6/°C |
| thermal conductivity | | ASTM C 177 | 0.2 W/m-°C |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Hardness (Rockwell R) | | ASTM D785 | 123 R |
| combustibility | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL fire rating V | | UL 94 | 1.5 mm |
| UL fire rating 5VB | | UL 94 | 2.49 mm |
| Limiting Oxygen Index (LOI) | | ASTM D 2863 | 32 % |
| Electrical Property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | 100000000000000000 ohm-cm |
| Surface Resistivity | | ASTM D257 | 10000000000000000 Ohm |
| dielectric constant | | ASTM D 150 | 3 |
| dielectric constant | | ASTM D 150 | 3 |
| Dissipation Factor | | ASTM D 150 | 50 E-4 |
| Dissipation Factor | | ASTM D 150 | 49 E-4 |
| Compared to the Leakage Traceability Index (CTI) | | UL 746A | PLC_0 |
| dielectric strength | in oil, 3.2 | ASTM D149 | 19.5 kV/mm |
| arc resistance | | ASTM D495 | PLC_6 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746A | PLC 2 |
| Hot wire ignition (HWI) | | UL 746A | PLC_1 |
| High current arc ignition (HAI) | | UL 746A | PLC_0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | Type I, 50，屈服 | ASTM D638 | 62 Mpa |
| elongation at break | Type I, 50 | ASTM D638 | 40 |
| bending strength | 2.6 mm/，屈服 | ASTM D790 | 102 Mpa |
| Flexural modulus | 2.6 mm/ | ASTM D790 | 2650 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 30℃ | ASTM D256 | 160 J/m |
| Impact strength of cantilever beam gap | 23℃ | ASTM D256 | 534 J/m |
| Instrumented dart impact energy -30 ℃ (-22 ℉) peak | | ASTM D3763 | 54 J |
| Instrumented dart impact energy 23 ℃ (73 ℉) total energy | | ASTM D3763 | 61 J |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.