برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.41 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 15 g/10min |
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 12.0 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.8 % |
| Shrinkage rate | MD | ISO 294-4 | 1.9 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 1.0 % |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.25 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 92 |
| Rockwell hardness | R计秤 | ISO 2039-2 | 120 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| burning rate | 1.00mm | ISO 3795 | 28 mm/min |
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| UL flame retardant rating | 0.75mm | IEC 60695-11-10,-20 | HB |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
| FMVSS flammability | | FMVSS302 | B |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Emissions of Organic Compounds | | VDA277 | 6.00 µgC/g |
| Emission | | VDA275 | <8.00 mg/kg |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Nominal tensile fracture strain | | ISO 527-2 | 25 % |
| Flexural modulus | | ISO 178 | 2900 Mpa |
| Tensile modulus | | ISO 527-2 | 3100 Mpa |
| tensile strength | 屈服 | ISO 527-2 | 67.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 15 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 290 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 350 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 9.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 9.0 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| relative permittivity | 100Hz | IEC 60250 | 4.20 |
| relative permittivity | 1MHz | IEC 60250 | 4.10 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 158 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 90.0 °C |
| vicat | | ISO 306/B50 | 160 °C |
| melting temperature | | ISO 11357-3 | 178 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| AnnealingTemperature | | | 160 °C |
| AnnealingTime-Optional | | | 30.0 min/mm |