برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Water absorption rate | 饱和,23°C | ASTM D570 | 0.070 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.070 % |
| density | | ASTM D792 | 1.02 g/cm³ |
| density | | ISO 1183 | 1.02 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 11 g/10min |
| Melt volume flow rate | 200°C/5.0kg | ISO 1133 | 12.0 cm³/10min |
| Shrinkage rate | MD | ASTM D955 | 0.65 % |
| Shrinkage rate | | ISO 294-4 | 0.30to1.0 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shore hardness | 邵氏D | ASTM D2240 | 75 |
| Shore hardness | 邵氏D | ISO 868 | 65 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| refractive index | | ASTM D542 | 1.573 |
| refractive index | | ISO 489 | 1.573 |
| transmissivity | 550nm | ASTM D1003 | 91.0 % |
| Haze ratio | | ASTM D1003 | 0.20 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ASTM D638 | 1640 MPa |
| Tensile modulus | | ISO 527-2 | 1550 MPa |
| tensile strength | 屈服,23°C | ASTM D638 | 25.5 MPa |
| tensile strength | 屈服,23°C | ISO 527-2 | 27.0 MPa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 2.0 % |
| elongation | Break | ASTM D638 | 220 % |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 180 % |
| Flexural modulus | | ASTM D790 | 1330 MPa |
| Flexural modulus | | ISO 178 | 1550 MPa |
| bending strength | | ASTM D790 | 27.2 MPa |
| bending strength | 5.0%应变 | | 31.0 MPa |
| bending strength | -- | ISO 178 | 31.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 3.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 32 J/m |
| Impact strength of cantilever beam gap | -30°C | ISO 180/A | 2.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 3.0 kJ/m² |
| InstrumentedDartImpact | Totalenergy | ASTM D3763 | 20.1 J |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| elongation | Break | ISO 527-3 | 180 % |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | >1.0E+15 ohms·cm |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric constant | 1.00mm,1MHz | ASTM D150 | 2.50 |
| dielectric constant | 100Hz | IEC 60250 | 2.50 |
| Dissipation Factor | 100Hz | IEC 60250 | 3E-04 |
| Dissipation Factor | 1MHz | IEC 60250 | 8E-04 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Surface Resistivity | | ASTM D257 | >1.0E+14 ohms |
| Surface Resistivity | | IEC 60093 | 1E+15 ohms |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 75.6 °C |
| Heat distortion temperature | 0.45MPa,Annealed，HDT | ISO 75-2/B | 75.0 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 60.0 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 58.0 °C |
| vicat | | ASTM D15253 | 87.8 °C |
| vicat | -- | ISO 306/A50 | 81.0 °C |
| vicat | -- | ISO 306/B50 | 51.0 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 1.3E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.0E-5to9.0E-5 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.