MPR 2380 BK USA Advanced
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.16 g/cm³ | |
| ISO 1183 | 1.16 g/cm³ | ||
| Apparent viscosity | 190°C,300sec^-1 | ASTM D3835 | 630 Pa·s |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shore hardness | Shore A | ASTM D2240 | 79 |
| Shore A | ISO 868 | 79 |
| elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| elongation | Break | ISO 37 | 550 % |
| tear strength | 24°C | ASTM D624 | 40.3 kN/m |
| 24°C | ISO 34-1 | 40 kN/m | |
| compression set | 24°C,22hr | ASTM D395A | 21 % |
| 100°C,22hr | ASTM D395A | 70 % | |
| 24°C,22hr | ISO 815 | 21 % | |
| 100°C,22hr | ISO 815 | 70 % | |
| Stretch permanent deformation | ASTM D412 | 13 % | |
| tensile strength | 100%应变 | ASTM D412 | 4.69 MPa |
| 100%应变 | ISO 37 | 4.69 MPa | |
| Yield | ASTM D412 | 11.0 MPa | |
| Yield | ISO 37 | 11.0 MPa | |
| elongation | Break | ASTM D412 | 550 % |
| aging | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| volume change | 100°C,168hr,inIRM903Oil#3 | ASTM D471 | 29 % |
| 100°C,168hr,在水中 | ASTM D471 | -10 % | |
| 100°C,168hr,inASTM#1Oil | ISO 1817 | 17 % | |
| 100°C,168hr,在水中 | ISO 1817 | -10 % | |
| Change rate of tensile strength in air | 125°C,168hr | ASTM D573 | 96 % |
| 100%Strain,125°C,168hr | ASTM D573 | 83 % | |
| 125°C,168hr | ISO 188 | 96 % | |
| 100%应变125°C,168hr | ISO 188 | 83 % | |
| volume change | 100°C,168hr,inASTM#1Oil | ASTM D471 | 17 % |
| 100°C,57120hr,inIRM903Oil#3 | ISO 1817 | 29 % |