TPU-Ester 2355-80AE TPU Lubrizol Advanced Materials, Inc.
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.18 g/cm³ | |
| melt mass-flow rate | 224°C/8.7kg | ASTM D1238 | 7.0 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.20to0.60 % |
| TD | ASTM D955 | 0.50to0.60 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shore hardness | Shore A | ASTM D2240 | 85 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Taber abraser | 1000g,H-22转轮 | ASTM D1044 | 10.0 mg |
| elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | 50%应变,3.20mm | ASTM D412 | 3.90 MPa |
| 100%应变,3.20mm | ASTM D412 | 6.20 MPa | |
| 300%应变,3.20mm | ASTM D412 | 15.2 MPa | |
| 断裂,3.20mm | ASTM D412 | 39.2 MPa | |
| elongation | 断裂,3.20mm | ASTM D412 | 550 % |
| elongation at break | 3.20mm | ASTM D412 | 60 % |
| tear strength | 3.20mm | ASTM D624 | 126 kN/m |
| compression set | 25°C,22hr | ASTM D395B | 25 % |
| 70°C,22hr | ASTM D395B | 75 % |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Glass Transition Temperature | DSC | -37.0 °C | |
| vicat | ASTM D15253 | 92.7 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 1.7E-04 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.