برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.35to1.45 g/cm³ |
| Apparent density | | ISO 60 | 0.55to0.70 g/cm³ |
| Shrinkage rate | MD1 | ISO 2577 | 0.60to0.80 % |
| Water absorption rate | 23°C,24hr | ISO 62 | <1.5 % |
| Shrinkage rate | | ISO 2577 | 0.40to0.60 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 3.60mm | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 900 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 900 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| compression stress | | ISO 604 | 200to250 MPa |
| Tensile modulus | Compression Molded | ISO 527-2 | 3000to5000 MPa |
| Tensile modulus | Injection | ISO 527-2 | 4000to6000 MPa |
| tensile strength | CompressionMolded | ISO 527-2 | 50.0to70.0 MPa |
| tensile strength | InjectionMolded | ISO 527-2 | 50.0to70.0 MPa |
| Flexural modulus | Compression Molded | ISO 178 | 6000to8000 MPa |
| Flexural modulus | Injection | ISO 178 | 6000to8000 MPa |
| bending strength | Compression Molded | ISO 178 | 70.0to90.0 MPa |
| bending strength | Injection | ISO 178 | 90.0to110 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO 179/1eA | 1.5to3.5 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO 179/1eA | 2.0to4.0 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO 179/1eU | 4.0to6.0 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO 179/1eU | 6.0to9.0 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Dissipation Factor | 1MHz | IEC 60250 | 0.060to0.080 |
| arc resistance | | ASTM D495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| Surface Resistivity | | IEC 60093 | 1.0E+13到1.0E+14 ohms |
| Volume resistivity | | IEC 60093 | 1.0E+16到1.0E+17 ohms·cm |
| dielectric strength | | IEC 60243-1 | 20to30 kV/mm |
| relative permittivity | 100Hz | IEC 60250 | 16.012.0 |
| relative permittivity | 1MHz | IEC 60250 | 6.004.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.60to0.80 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD：50到150°C | ISO 11359-2 | 2.5E-5到3.5E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.20to0.40 W/m/K |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.