برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.06 g/cm³ |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 3.0 g/10min |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.40to0.70 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 106 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| elongation | 断裂,3.20mm | ASTM D638 | 20 % |
| Flexural modulus | 3.20mm | ASTM D790 | 2350 MPa |
| bending strength | 3.20mm | ASTM D790 | 73.5 MPa |
| tensile strength | 屈服,3.20mm | ASTM D638 | 47.1 MPa |
| Tensile strain | Yield,3.20mm | ASTM D638 | >5.0 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | -30°C,3.20mm | ASTM D256 | 78 J/m |
| Impact strength of cantilever beam gap | -30°C,6.40mm | ASTM D256 | 69 J/m |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 160 J/m |
| Impact strength of cantilever beam gap | 23°C,6.40mm | ASTM D256 | 150 J/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | 23°C | ASTM D257 | 1.5E+03 ohms·cm |
| dielectric strength | 23°C | ASTM D149 | 33 kV/mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| vicat | | ASTM D15254 | 115 °C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 116 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 107 °C |