impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	50	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	50	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Burning wire flammability index	1.5mm	IEC 60695-2-12	700	°C
Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	800	°C
Hot filament ignition temperature	1.5mm,Passes	IEC 60695-2-13	825	°C
Hot filament ignition temperature	Hot filament ignition temperature	3.0mm,Passes	IEC 60695-2-13	800	°C
Burning rate		ISO 3795	25	mm/min
UL flame retardant rating	1.6mm	IEC 60695-11-10,-20	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	IEC 60695-11-10,-20	HB
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus		ISO 527-2/1A/1	15500	Mpa
tensile strength	Break	ISO 527-2/1A/5	160	Mpa
Tensile strain	Break	ISO 527-2/1A/5	1.7	%
Bending modulus		ISO 178	16000	Mpa
bending strength		ISO 178	250	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	225	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	208	°C
Vicat softening temperature	--	ISO 306/A50	214	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	198	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Melt Volume Flow Rate (MVR)	260°C/2.16kg	ISO 1133	11.0	cm3/10min
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.25	%