EVA UE632 Taiwan Polymer

ویژگی‌ها:

It has the characteristics of softness elasticity transparency and non toxicity as well as excellent resistance to external stress cracking impact strength and low-temperature flexibility. It is easy to process

کاربردهای معمول:

After adding crosslinking agents and foaming agents foam shoe soles are manufactured by compression molding or injection molding

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

کاربردهای معمول:	After adding crosslinking agents and foaming agents \| foam shoe soles are manufactured by compression molding or injection molding
ویژگی‌ها:	It has the characteristics of softness \| elasticity \| transparency \| and non toxicity \| as well as excellent resistance to external stress cracking \| impact strength \| and low-temperature flexibility. It is easy to process

گواهی‌نامه‌ها

No Data...

برگه داده فنی

Basic Performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Vinyl acetate content		USIFE	22	%
density		ASTM D-1505	0.942	g/cm3
melt mass-flow rate		ASTM D-1238	2.2	g/10min
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength	模片，Break	ASTM D-638	170	kg/cm2
Elongation at Break	模片	ASTM D-638	820	%
Shore hardness		ASTM D-2240	34
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Low temperature brittleness resistance	F50	ASTM D-746	＜-76	℃
Vicat softening temperature		ASTM D-1525	58	℃
Melting temperature		USI Method	82	℃

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.