MMW-HDPE TOTAL Polyethylene HDPE 5908 TOTAL
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 0.959 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.80 g/10min |
| 190°C/21.6kg | ASTM D1238 | 22 g/10min |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| gloss | ASTM D523 | 50 | |
| Haze ratio | ASTM D1003 | 15 % |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | MD:断裂,25µm | ASTM D882A | 62.1 MPa |
| Elmendorf tear strength | TD:25µm | ASTM D1922 | 390 g |
| Water Vapor Transmission Rate | 38°C,25µm | ASTME96 | 7.8 g/m²/24hr |
| film thickness | 25 µm | ||
| Secant modulus | 1%正割,MD:25µm | ASTM D882A | 1030 MPa |
| 2%正割,MD:25µm | ASTM D882A | 689 MPa | |
| 1%正割,TD:25µm | ASTM D882A | 883 MPa | |
| 2%正割,TD:25µm | ASTM D882A | 703 MPa | |
| tensile strength | MD:屈服,25µm | ASTM D882A | 31.0 MPa |
| TD:屈服,25µm | ASTM D882A | 31.0 MPa | |
| TD:断裂,25µm | ASTM D882A | 24.1 MPa | |
| elongation | MD:断裂,25µm | ASTM D882A | 600 % |
| TD:断裂,25µm | ASTM D882A | 300 % | |
| Elmendorf tear strength | MD:25µm | ASTM D1922 | 24 g |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melting temperature | ASTM D3417 | 135 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.