Copolyester MN052 Eastman Chemical Company

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23°C	ASTM D256	51 J/m
	Impact strength of cantilever beam gap	-40°C	ASTM D4218	NoBreak
		Impact strength of cantilever beam gap	23°C	ASTM D4218	NoBreak
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-40°C	ASTM D256	36 J/m

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Yield,23°C	ASTM D638	57.0 MPa
tensile strength	tensile strength	Break,23°C	ASTM D638	26.0 MPa
elongation	Yield,23°C	ASTM D638	4.0 %
Bending modulus	23°C	ASTM D790	2500 MPa
bending strength	Yield,23°C	ASTM D790	81.0 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	66.0 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	62.0 °C
Vicat softening temperature		ASTM D15252	79.0 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.32 g/cm³
Shrinkage rate	MD：3.20mm	ASTM D955	0.40 %
Water absorption rate	23°C,24hr	ASTM D570	0.10 %

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Dissipation factor	23°C,1kHz	ASTM D150	8E-03
Dielectric strength	23°C	ASTM D149	16 kV/mm
Dielectric constant	23°C,1kHz	ASTM D150	3.20
Dielectric constant	Dielectric constant	23°C,1MHz	ASTM D150	3.00
Dissipation factor	23°C,1MHz	ASTM D150	0.020
Arc resistance		ASTM D495	155 sec

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	R-Sale,23°C	ASTM D785	110