PA66 Staramide AG6K EUROSTAR FRANCE

ویژگی‌ها:

Filler glass fiber reinforced material 30% filler by weight

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

ویژگی‌ها:

Filler | glass fiber reinforced material | 30% | filler by weight

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	6.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-40°C	ISO 180/1A	6.0	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	60	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	55	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	7.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	6.0	kJ/m²
Impact strength of cantilever beam gap	-20°C	ISO 180/1A	7.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.0	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Burning wire flammability index	2.0mm	IEC 60695-2-12	650	°C
UL flame retardant rating	3.0mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	0.75mm	UL 94	HB
Burning rate	3.00mm	FMVSS302	2.0	mm/min
Extreme Oxygen Index		ISO 4589-2	26	%
Burning rate	2.00mm	FMVSS302	6.0	mm/min
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
bending strength		ISO 178	260	MPa
Tensile strain	Break	ISO 527-2/5	3.0	%
Bending modulus		ISO 178	9000	MPa
Tensile modulus		ISO 527-2/1	9400	MPa
tensile strength	Break	ISO 527-2/5	170	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
RTI		UL 746	120	°C
RTI Imp		UL 746	95.0	°C
RTI Elec		UL 746	110	°C
thermal conductivity		ISO 8302	0.33	W/m/K
Linear coefficient of thermal expansion	TD:23to60°C	ISO 11359-2	7.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:23to60°C	ISO 11359-2	2.5E-05	cm/cm/°C
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Vicat softening temperature	--	ISO 306/B120	258	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	260	°C
Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	260	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	248	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density		ISO 1183	1.37	g/cm³
Shrinkage rate	MD	Internal Method	0.20to0.40	%
Water absorption rate	Saturation,23°C	ISO 62	4.5	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.2	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 1
Compared to the anti leakage trace index	Compared to the anti leakage trace index	--	IEC 60112	PLC 1
Dissipation factor	1MHz	IEC 60250	0.016
	Dissipation factor	60Hz	IEC 60250	7E-03
	Dissipation factor	Dissipation factor	50Hz	IEC 60250	7E-03
Relative permittivity	1MHz	IEC 60250	3.20
Volume resistivity		IEC 60093	>1.0E+16	ohms·cm
Dielectric strength	3.20mm,in Oil	IEC 60243-1	20	kV/mm
Relative permittivity	50Hz	IEC 60250	3.40
Relative permittivity	Relative permittivity	60Hz	IEC 60250	3.40
Surface resistivity		IEC 60093	>1.0E+16	ohms
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	L-Sale	ISO 2039-2	113