EHMWPE BSR Crown Plastics
0
- ویژگی‌ها:Mechanical properties
مقایسهبرگه داده فنی
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| tensile strength | 断裂,0.762mm | ASTM D638 | 53.0 MPa |
| 断裂,1.52mm | ASTM D638 | 49.0 MPa | |
| melting temperature | --2 | 136 °C | |
| Linear coefficient of thermal expansion | MD：-100到-20°C,3.18mm | ASTM D696 | 9.2E-04 cm/cm/°C |
| MD：20到100°C,3.18mm | ASTM D696 | 1.5E-04 cm/cm/°C | |
| Surface Resistivity | 0.762mm | ASTM D257 | 1E+03 ohms |
| 1.52mm | ASTM D257 | 1E+03 ohms | |
| 3.18mm | ASTM D257 | 1E+03 ohms | |
| Volume resistivity | 0.762mm | ASTM D257 | 6E+07 ohms·cm |
| Dissipation Factor | 3.18mm,10kHz | ASTM D150 | 0.0 |
| 3.18mm,5MHz | ASTM D150 | -1E-03 | |
| StaticDecay | 762.0µm | <10 msec | |
| 1.52mm | <10 msec | ||
| 3.18mm | <10 msec | ||
| tensile strength | 断裂,3.18mm | ASTM D638 | 44.0 MPa |
| elongation | 断裂,0.762mm | ASTM D638 | 60 % |
| 断裂,1.52mm | ASTM D638 | 460 % | |
| 断裂,3.18mm | ASTM D638 | 470 % | |
| coefficient of friction | 与钢-动态3 | ASTM D1894 | 0.10to0.22 |
| 与钢-动态4 | ASTM D1894 | 0.050to0.10 | |
| 与钢-动态5 | ASTM D1894 | 0.050to0.080 | |
| 与自身-动态2 | ASTM D1894 | 0.14 | |
| 与自身-动态6 | ASTM D1894 | 0.13 | |
| 与自身-动态7 | ASTM D1894 | 0.14 | |
| 与自身-静态2 | ASTM D1894 | 0.16 | |
| 与自身-静态6 | ASTM D1894 | 0.16 | |
| 与自身-静态7 | ASTM D1894 | 0.16 | |
| Impact strength of cantilever beam gap | 3.18mm | ASTM D256 | 80 J/m |
| melting temperature | --6 | 134 °C | |
| density | ASTM D792 | 0.930 g/cm³ | |
| Crystallinity | 762.0µm | ASTM D3417 | 48 % |
| 1.52mm | ASTM D3417 | 47 % | |
| 3.18mm | ASTM D3417 | 50 % | |
| relative viscosity | 762.0µm | ASTM D4020 | 230to350 cm³/g |
| 1.52mm | ASTM D4020 | 230to350 cm³/g | |
| tensile strength | 屈服,0.762mm | ASTM D638 | 23.0 MPa |
| 屈服,1.52mm | ASTM D638 | 20.0 MPa | |
| 屈服,3.18mm | ASTM D638 | 22.0 MPa | |
| relative viscosity | 3.18mm | ASTM D4020 | 230to350 cm³/g |
| Shore hardness | 邵氏D,0.762mm | ASTM D2240 | 65 |
| 邵氏D,1.52mm | ASTM D2240 | 65 | |
| 邵氏D,3.18mm | ASTM D2240 | 65 | |
| Volume resistivity | 1.52mm | ASTM D257 | 1.5E+07 ohms·cm |
| 3.18mm | ASTM D257 | >2.0E+7 ohms·cm | |
| dielectric strength | 3.18mm | ASTM D149 | 14 kV/mm |
| dielectric constant | 0.762mm | ASTM D150 | 2.39 |
| 1.52mm | ASTM D150 | 2.29 | |
| 3.18mm | ASTM D150 | 2.28 | |
| Dissipation Factor | 0.762mm,10kHz | ASTM D150 | -1E-03 |
| 0.762mm,5MHz | ASTM D150 | -1E-03 | |
| 1.52mm,10kHz | ASTM D150 | -2E-03 | |
| 1.52mm,5MHz | ASTM D150 | -1E-03 | |
| Tensile modulus | 0.762mm | ASTM D638 | 725 MPa |
| 1.52mm | ASTM D638 | 731 MPa | |
| 3.18mm | ASTM D638 | 672 MPa |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.