ABS+PBT Infino VB-3100G LOTTE KOREA
0
مقایسهبرگه داده فنی
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ISO 2577 | 0.60to1.2 % |
| Water absorption rate | 平衡,23°C | ASTM D570 | 0.080 % |
| 平衡,23°C,50%RH | ISO 62 | 0.080 % | |
| tensile strength | Yield | ASTM D638 | 74.0 MPa |
| bending strength | ISO 178 | 90.0 MPa | |
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 49 J/m |
| 23°C | ISO 180/1A | 4.0 kJ/m² | |
| tensile strength | Yield | ISO 527-2/5 | 70.0 MPa |
| elongation | Break | ASTM D638 | 4.0 % |
| Tensile strain | Break | ISO 527-2/5 | 4.0 % |
| Flexural modulus | ASTM D790 | 3900 MPa | |
| ISO 178 | 3500 MPa | ||
| bending strength | ASTM D790 | 98.0 MPa | |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| Rockwell hardness | R-Scale | ASTM D785 | 113 |
| R-Scale | ISO 2039-2 | 113 | |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 135 °C |
| 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 125 °C | |
| vicat | -- | ISO 306/B50 | 147 °C |
| -- | ISO 306/B120 | 151 °C | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| density | ASTM D792 | 1.45 g/cm³ | |
| ISO 1183 | 1.45 g/cm³ | ||
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 30 g/10min |
| 250°C/2.16kg | ISO 1133 | 30 g/10min | |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.60to1.2 % |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.