برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | g/cm³ | 1.14 -- |
| Water absorption rate | 23°C,24hr | % | 0.59 -- |
| Water absorption rate | 饱和,23°C | % | 6.3 -- |
| Water absorption rate | 平衡,23°C,50%RH | % | 2.0 -- |
| Water absorption rate | 23°C,3.00mm2 | mg | 40.0 -- |
| Water absorption rate | 23°C,3.00mm3 | mg | 76.01.1 -- |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| ball-indentation hardness | 10.0mm | MPa | 150 -- |
| Rockwell hardness | M计秤,10.0mm | | 81 -- |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 3.0mm | | HB -- |
| UL flame retardant rating | 6.0mm | | HB -- |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | MPa | 3150 1530 |
| tensile strength | Yield | MPa | 78.0 50.0 |
| tensile strength | -- | MPa | 80.0 -- |
| Tensile strain | Yield | % | 5.0 -- |
| Tensile strain | Break | % | 25 >50 |
| compression stress | 1%应变 | MPa | 31.0 -- |
| compression stress | 2%应变 | MPa | 59.0 -- |
| compression stress | 5%应变 | MPa | 87.0 -- |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 3.5 -- |
| Impact strength of simply supported beam without notch | | kJ/m² | 75 -- |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| relative permittivity | 100Hz | | 3.60 6.60 |
| relative permittivity | 1MHz | | 3.20 3.70 |
| Dissipation Factor | 100Hz | | 0.012 0.14 |
| Dissipation Factor | 1MHz | | 0.016 0.050 |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 0 |
| Surface Resistivity | | ohms | >1.0E+13 >1.0E+12 |
| Volume resistivity | | ohms·cm | >1.0E+14 >1.0E+12 |
| dielectric strength | 1.00mm,在油中 | kV/mm | 25 17 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD：23到60°C | cm/cm/°C | 8E-05 -- |
| Linear coefficient of thermal expansion | MD：23到100°C | cm/cm/°C | 9.5E-05 -- |
| thermal conductivity | 23°C | W/m/K | 0.29 -- |
| Minimum operating temperature | | °C | -30 -- |
| maximum service temperature | continuously:for20,000h | °C | 90 -- |
| maximum service temperature | continuously:for5,000h | °C | 105 -- |
| maximum service temperature | forshortperiods | °C | 165 -- |
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 75.0 -- |
| melting temperature | | °C | 215 -- |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.
مقایسه