برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.42 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 25 g/10min |
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 21.0 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.9 % |
| Shrinkage rate | MD | ISO 294-4 | 1.9 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 1.4 % |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.40 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 92 |
| Rockwell hardness | R计秤 | ISO 2039-2 | 120 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| burning rate | 1.00mm | ISO 3795 | 20 mm/min |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| UL flame retardant rating | 0.8mm | IEC 60695-11-10,-20 | HB |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
| Limiting Oxygen Index | | ISO 4589-2 | 23 % |
| FMVSS flammability | | FMVSS302 | B |
| atomization | F-value(refraction) | ISO 6452 | 95 % |
| atomization | G-value(condensate) | ISO 6452 | 2E-04 g |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Emissions of Organic Compounds | | VDA277 | 4.30 µgC/g |
| Emission | | VDA275 | <8.00 mg/kg |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 7.0 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 200 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 200 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 8.0 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Nominal tensile fracture strain | | ISO 527-2 | 23 % |
| Tensile creep modulus | 1hr | ISO 899-1 | 2800 Mpa |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1500 Mpa |
| Flexural modulus | | ISO 178 | 3000 Mpa |
| coefficient of friction | vs.Itself-Dynamic,1hr | ASTM D1894 | 0.25 |
| Tensile modulus | | ISO 527-2 | 3300 Mpa |
| tensile strength | 屈服 | ISO 527-2 | 71.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 12 % |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | 1E+14 ohms·cm |
| relative permittivity | 100Hz | IEC 60250 | 3.80 |
| relative permittivity | 1MHz | IEC 60250 | 3.80 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Hot wire ignition (HWI) | 0.750mm | UL 746 | PLC 4 sec |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 162 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 94.0 °C |
| vicat | | ISO 306/B50 | 160 °C |
| melting temperature | | ISO 11357-3 | 178 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ASTME831 | 1E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| AnnealingTemperature | | | 160 °C |
| AnnealingTime-Optional | | | 30.0 min/mm |
| Effective thermal diffusivity coefficient | | | 8E-08 m²/s |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.
مقایسه
مشاهده قیمت‌ها