برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 5.0 g/10min |
| melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 19 g/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.10-0.30 % |
| Water absorption rate | 24hr | ASTM D570 | 0.14 % |
| Water absorption rate | 平衡,23°C | ASTM D570 | 0.26 % |
| Specific volume | | ASTM D792 | 0.697 cm³/g |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M计秤 | ASTM D785 | 92 |
| Rockwell hardness | R计秤 | ASTM D785 | 120 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| UL flame retardant rating | 1.5mm | UL 94 | V-1 |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 断裂 | ASTM D638 | 100 Mpa |
| elongation | 断裂 | ASTM D638 | 2.0 % |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 6610 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 153 Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 24.0 mg |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Dart impact | 23°C | ASTM D3029 | 5.00 J |
| Impact strength of cantilever beam gap | | ASTM D1822 | 67.0 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Dissipation Factor | 50Hz | ASTM D150 | 1.1E-03 |
| Dissipation Factor | 60Hz | ASTM D150 | 1.1E-03 |
| Dissipation Factor | 1MHz | ASTM D150 | 7E-03 |
| arc resistance | | ASTM D495 | PLC7 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 5 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 4 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 0 |
| Volume resistivity | | ASTM D257 | >1.0E+17 ohms·cm |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 19 KV/mm |
| dielectric constant | 50Hz | ASTM D150 | 3.35 |
| dielectric constant | 60Hz | ASTM D150 | 3.35 |
| dielectric constant | 1MHz | ASTM D150 | 3.31 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| specific heat | | ASTMC351 | 1130 J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.22 W/m/K |
| RTI Elec | | UL 746 | 120 °C |
| RTI Imp | | UL 746 | 120 °C |
| RTI Str | | UL 746 | 130 °C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 151 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 146 °C |
| vicat | | ASTM D15255 | 165 °C |
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 2.2E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.