impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dart impact	-30°C	ASTM D3029	24.0	J
Dart impact	Dart impact	-40°C	ASTM D3029	13.0	J
Impact strength of cantilever beam gap	23°C	ASTM D256	390	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-40°C	ASTM D256	160	J/m
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	1.5 mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	V-0
Radiation board grade		UL Unspecified	TRUE
squeeze out	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
drying temperature			90 to 100	°C
drying time			2.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Temperature in Zone 1 of the material cylinder			170	°C
Temperature in Zone 2 of the material cylinder			170	°C
Temperature in Zone 3 of the material cylinder			190	°C
Temperature in Zone 4 of the material cylinder			190	°C
Joint temperature			205	°C
Melt Temperature			195 to 210	°C
Oral mold temperature			205	°C
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
bending strength	Yield, 100 mm Span	ASTM D790	67.0	Mpa
Bending modulus	100 mm Span	ASTM D790	2270	Mpa
elongation	Break	ASTM D638	50	%
tensile strength	Yield	ASTM D638	42.0	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
RTI		UL 746	50.0	°C
RTI Imp		UL 746	50.0	°C
RTI Elec		UL 746	50.0	°C
Linear coefficient of thermal expansion	-40 to 95°C，Flow	ASTM E831	7.4E-5	cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	82.0	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	93.0	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Water absorption rate	24 hr	ASTM D570	0.070	%
density		ASTM D792	1.08	g/cm³
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Compared to the anti leakage trace index		UL 746	PLC 2
Arc resistance		ASTM D495	PLC 7
Dissipation factor	1 MHz	IEC 60250	3.5E-3
	Dissipation factor	60 Hz	ASTM D150	4.0E-3
	Dissipation factor	Dissipation factor	50 Hz	ASTM D150	4.0E-3
Dielectric constant	50 kHz	ASTM D150	2.80
Dielectric constant	Dielectric constant	60 Hz	ASTM D150	2.80
Dielectric strength	3.20 mm, in Oil	ASTM D149	25	KV/mm
High arc combustion index		UL 746	PLC 0
High voltage arc tracing rate		UL 746	PLC 4
Hot wire ignition		UL 746	PLC 1
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	R-Scale	ASTM D785	113