optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Refractive index		ASTM D542，ISO 489	1.586
Transmittance rate	2540 μm	ASTM D1003	88.0 to 90.0	%
turbidity	2540 μm	ASTM D1003	< 0.80	%
impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of cantilever beam gap	23℃	ASTM D256	800	J/m
	Impact strength of cantilever beam gap	-30℃，80103	ISO 180-1A	12	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃，80103	ISO 180-1A	70	kJ/m²
Suspended wall beam without notch impact strength	23℃	ASTM D4812	无断裂	J/m
	Suspended wall beam without notch impact strength	23℃，80103	ISO 180/1U	无断裂	kJ/m²
	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30℃，80103	ISO 180/1U	无断裂	kJ/m²
Dart impact	23℃	ASTM D3763	65	J
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	R-Scale	ASTM D785	120
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	120
Tensile modulus	50 mm/min	ASTM D638	2350	Mpa
Tensile modulus	Tensile modulus	1 mm/min	ISO 527	2350	Mpa
tensile strength	Yield，I型，50 mm/min	ASTM D638	63	Mpa
tensile strength	tensile strength	Yield，50 mm/min	ISO 527	63	Mpa
Tensile strain	Yield，I型，50 mm/min	ASTM D638	6	%
	Tensile strain	Yield，50 mm/min	ISO 527	6	%
		Tensile strain	Break，I型，50 mm/min	ASTM D638	> 70	%
		Tensile strain	Tensile strain	Break，50 mm/min	ISO 527	> 70	%
Bending modulus	1.3 mm/min，50 mmSpan	ASTM D790	2300	Mpa
Bending modulus	Bending modulus	2 mm/min	ISO 178	2300	Mpa
bending strength	Yield，1.3 mm/min，50 mmSpan	ASTM D790	90	Mpa
bending strength	bending strength	Yield，2 mm/min	ISO 178	90	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45 MPa，3.2 mm	ASTM D648	138	°C
	Hot deformation temperature	0.45 MPa， 80104，64 mmSpan	ISO 75-2/Bf	138	°C
		Hot deformation temperature	1.8 MPa，3.2 mm	ASTM D648	127	°C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa， 80104，64 mmSpan	ISO 75-2/Af	127	°C
Vicat softening temperature	B50	ISO 306	143	°C
Vicat softening temperature	Vicat softening temperature	B50	ASTM D1525	143	°C
Ball indentation test	125℃+/- 2℃	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD，-40℃~95℃	ASTM E831	0.000070	1/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD，23℃~80℃	ISO 11359-2	0.000070	1/℃
thermal conductivity		ASTM C177	0.2	W/m/℃
thermal conductivity	thermal conductivity		ISO 8302	0.2	W/m/℃
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density		ASTM D792	1.2	g/cm³
melt mass-flow rate	300℃，1.20kg	ASTM D1238	10	g/10min
Melt Volume Flow Rate (MVR)	300℃，1.2 kg	ISO 1133	9	cm3/10min
Shrinkage rate	MD	Internal Method	0.50 - 0.70	%
Shrinkage rate	Shrinkage rate	MD：3.2 mm	Internal Method	0.50 - 0.70	%
Water absorption rate	Saturation，23℃	ISO 62	0.35	%
Water absorption rate	Water absorption rate	Equilibrium，23℃	ASTM D570	0.35	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Volume resistivity		ASTM D257，IEC 60093	> 1.0E+15	ohms·cm
Dielectric strength	1.6 mm	ASTM D149，IEC 60243-1	27	KV/mm
Dielectric constant	60 Hz	ASTM D150	3
Dielectric constant	Dielectric constant	1 MHz	ASTM D150	3
Dissipation factor	60 Hz	ASTM D150	0.001
Dissipation factor	Dissipation factor	1 MHz	ASTM D150	0.01