برگه داده فنی
physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Water absorption rate | 23°C,24hr,0.254mm | ASTM D570 | 0.50 % |
optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
transmittance | 250.0µm,UV | | 89 % |
gloss | 60°,250µm | ASTM D2457 | 158 |
refractive index | | ASTM D542 | 1.540 |
transmittance | 250µm | ASTM D1003 | 93.0 % |
Haze ratio | 250µm | ASTM D1003 | 0.80 % |
Yellowness Index | 250mm | ASTM D1925 | 0.50 YI |
Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
SurfaceEnergy | Dispersive:23°C,250.0µm | ASTM D5946 | 39 dyne/cm |
SurfaceEnergy | Polar:23°C,250.0µm | ASTM D5946 | 8 dyne/cm |
SurfaceEnergy | Total:23°C,250.0µm | ASTM D5946 | 47 dyne/cm |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Taber wear resistance | 23°C,250.0µm | ASTM D1044 | 20Haze % |
elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
tear strength | Split6 | ASTM D1938 | 9.0 kN/m |
tear strength | Split7 | ASTM D1938 | 10 kN/m |
film | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Dart impact | -30°C,250µm | ASTM D1709A | 830 g |
Dart impact | -18°C,250µm | ASTM D1709A | 830 g |
Dart impact | 23°C,250µm | ASTM D1709A | 830 g |
Tear resistance of pants | MD:250µm | ISO 6383-1 | 10.0 N/mm |
Tear resistance of pants | TD:250µm | ISO 6383-1 | 9.00 N/mm |
OTr | 23°C,250µm,50%RH | ASTM D3985 | 44 cm³·mm/m²/atm/24hr |
Water Vapor Transmission Rate | 23°C,100%RH,250µm | ASTMF1249 | 4.0 g/m²/24hr |
Water Vapor Transmission Rate | 38°C,100%RH,250µm | ASTMF1249 | 10 g/m²/24hr |
Carbon dioxide transmittance | 23°C,254.0µm | ASTM D1434 | 210 cm³·mm/m²/atm/24hr |
Elmendorf tear strength | MD:23°C,250.0µm | ASTM D1922 | 4 N |
film thickness | | | 250 µm |
Thin film puncture strength | 250µm | ASTM D3763 | 4.50 J |
Secant modulus | 250µm,MD | ASTM D882 | 1500 Mpa |
Secant modulus | 250µm,TD | ASTM D882 | 1400 Mpa |
tensile strength | Yield,250μm | ASTM D882 | 43.0 Mpa |
tensile strength | Yield,250µm,TD | ASTM D882 | 41.0 Mpa |
tensile strength | Break,250µm,MD | ASTM D882 | 57.0 Mpa |
tensile strength | Break,250µm,TD | ASTM D882 | 42.0 Mpa |
Tensile strain | Yield,250µm,MD | ASTM D882 | 8.0 % |
Tensile strain TD | Yield,250µm | ASTM D882 | 8.0 % |
elongation | Break,250μm | ASTM D882 | 110 % |
Tensile strain TD | Break,250µm | ASTM D882 | 120 % |
Elmendorf tear strength | TD:23°C,250.0µm | ASTM D1922 | 4 N |
PPTTearResistance | MD:23°C,250.0µm | | 40 N |
PPTTearResistance | TD:23°C,250.0µm | | 40 N |
tear strength | MD:23°C,250.0µm | ASTM D1938 | 310 gf |
tear strength | TD:23°C,250.0µm | ASTM D1938 | 200 gf |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
specific heat | 60°C | DSC | 1700 J/kg/°C |
specific heat | 100°C | DSC | 1900 J/kg/°C |
specific heat | 150°C | DSC | 2300 J/kg/°C |
specific heat | 200°C | DSC | 2400 J/kg/°C |
specific heat | 250°C | DSC | 2600 J/kg/°C |
melting temperature | | | 119 °C |
Linear coefficient of thermal expansion | MD:23°C | ASTM D696 | 8E-05 cm/cm/°C |