PC+TPU Texin® 4210 Covestro - Polycarbonates

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	MD：2.54mm	ASTM D955	0.80 %
density		ASTM D792	1.21 g/cm³
density	density		ISO 1183	1.21 g/cm³
Shrinkage rate	TD：2.54mm	ASTM D955	0.80 %
	Shrinkage rate	TD:2.54mm	ISO 2577	0.80 %
	Shrinkage rate	Shrinkage rate	MD:2.54mm	ISO 2577	0.80 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Shore hardness	邵氏D	ASTM D2240	70
Shore hardness	Shore hardness	邵氏D	ISO 868	70

Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون
CompressiveLoad	10%Deflection	ASTM D575	31.7 MPa
	CompressiveLoad	15%Deflection	ASTM D575	41.4 MPa
		CompressiveLoad	2%Deflection	ASTM D575	3.45 MPa
			CompressiveLoad	20%Deflection	ASTM D575	56.5 MPa
				CompressiveLoad	25%Deflection	ASTM D575	68.9 MPa
					CompressiveLoad	5%Deflection	ASTM D575	13.8 MPa
					CompressiveLoad	CompressiveLoad	50%Deflection	ASTM D575	130 MPa

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Flexural modulus	23°C	ASTM D790	700 MPa
Flexural modulus	Flexural modulus	23°C	ISO 178	700 MPa
Taber abraser	1000Cycles,1000g,H-18转轮	ISO 4649	65.0 mg
Taber abraser	Taber abraser	1000Cycles,1000g,H-18转轮	ASTM D1044	65.0 mg

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	-30°C,3.18mm	ASTM D256	53 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	850 J/m

elastomer	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Yield	ASTM D412	40.0 MPa
tensile strength	tensile strength	Yield	ISO 37	40.0 MPa
elongation	Break	ASTM D412	130 %
elongation	elongation	Break	ISO 37	130 %
tear strength		ASTM D624	158 kN/m
tear strength	tear strength		ISO 34-1	160 kN/m
Shore hardness		ASTM D2632	45 %

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,未退火，HDT	ASTM D648	98.0 °C
	Heat distortion temperature	0.45MPa,未退火，HDT	ISO 75-2/B	98.0 °C
		Heat distortion temperature	1.8MPa,未退火，HDT	ASTM D648	59.0 °C
		Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火，HDT	ISO 75-2/A	59.0 °C
brittle temperature		ASTM D746	<-68.0 °C
brittle temperature	brittle temperature		ISO 974	<-68.0 °C
Glass Transition Temperature		DMA	-35.0 °C
vicat		ASTM D15253	139 °C
vicat	vicat		ISO 306/50	139 °C
Linear coefficient of thermal expansion	MD	ASTM D696	1E-04 cm/cm/°C