PP Homopolymer BFI 4170 Blueridge Films Inc.
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D1505 | 0.905 g/cm³ | |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 0.75 g/10min |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Dart impact | Blown Film | ASTM D1709A | 350 g |
| Elmendorf tear strength | MD:吹塑薄膜 | ASTM D1922 | 55 g |
| TD:吹塑薄膜 | ASTM D1922 | 300 g | |
| OTr | 23°C,吹塑薄膜,0%RH | ASTM D3985 | 53 cm³·mm/m²/atm/24hr |
| Water Vapor Transmission Rate | 38°C,吹塑薄膜,100%RH | ASTMF1249 | 0.18 g·mm/m²/atm/24hr |
| Secant modulus | 2%正割,MD:吹塑薄膜 | ASTM D882 | 689 MPa |
| 2%正割,TD:吹塑薄膜 | ASTM D882 | 600 MPa | |
| tensile strength | MD:屈服,吹塑薄膜 | ASTM D882 | 26.2 MPa |
| TD:屈服,吹塑薄膜 | ASTM D882 | 24.8 MPa | |
| MD:断裂,吹塑薄膜 | ASTM D882 | 58.6 MPa | |
| TD:断裂,吹塑薄膜 | ASTM D882 | 37.9 MPa | |
| elongation | MD:断裂,吹塑薄膜 | ASTM D882 | 750 % |
| TD:断裂,吹塑薄膜 | ASTM D882 | 770 % |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melting temperature | DSC | 160to165 °C |