PET Skyrol® SL10 SK Chemicals
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D1505 | 1.40 g/cm³ | |
| Shrinkage rate | MD:150°C,30分钟,0.0120mm | 内部方法 | 1.7 % |
| MD:150°C,30分钟,0.0200mm | 内部方法 | 1.7 % | |
| TD:150°C,30分钟,0.0120mm | 内部方法 | 0.60 % | |
| TD:150°C,30分钟,0.0200mm | 内部方法 | 0.50 % |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Haze ratio | 12.0µm | ASTM D1003 | 3.1 % |
| 20.0µm | ASTM D1003 | 3.9 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| coefficient of friction | 与自身-动态4 | ASTM D1894 | 0.40 |
| 与自身-动态3 | ASTM D1894 | 0.40 | |
| 与自身-静态4 | ASTM D1894 | 0.60 | |
| --3 | ASTM D1894 | 0.50 |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | MD:屈服,12µm | ASTM D882 | 234 MPa |
| MD:屈服,20µm | ASTM D882 | 221 MPa | |
| TD:屈服,12µm | ASTM D882 | 200 MPa | |
| TD:屈服,20µm | ASTM D882 | 200 MPa | |
| elongation | TD:断裂,12µm | ASTM D882 | 130 % |
| TD:断裂,20µm | ASTM D882 | 140 % | |
| MD:断裂,12µm | ASTM D882 | 130 % | |
| MD:断裂,20µm | ASTM D882 | 140 % |