PA66 20G6201 Changchun Chemical (Zhangzhou)
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| ash content | 30 % | ||
| 30 % | |||
| Shrinkage rate | D955 | 0.3-0.8 % | |
| density | D792 | 1.35 g/cm³ |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | ASTM D638 | 1700 kg/c㎡ | |
| D638 | 167 MPa | ||
| bending strength | D790 | 235 MPa | |
| Flexural modulus | D790 | 7840 MPa | |
| Impact strength of cantilever beam gap | D256 | 14 kg·cm/cm |
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| density | ASTM D792 | 1.35 - | |
| melting temperature | ASTM DSC | 264 ℃ | |
| Shrinkage rate | ASTM D955 | 0.3-0.8 % | |
| bending strength | ASTM D790 | 2400 kg/c㎡ | |
| Flexural modulus | ASTM D790 | 80000 kg/c㎡ | |
| Impact strength of cantilever beam gap | ASTM D256 | 14 ㎏.㎝/㎝ | |
| Compared to the Leakage Tracking Index (CTI) | ASTM D3638 | PLC 0 |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| dielectric strength | D149 | 25 kv/mm | |
| Compared to the Leakage Tracking Index (CTI) | D3638 | PLC 0 | |
| dielectric strength | ASTM D149 | 25 kV/㎜ |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa，HDT | D648 | 256 ℃ |
| melting temperature | DSC | 264 ℃ | |
| Heat distortion temperature | 1.8MPa，HDT | D648 | 249 ℃ |
| 18.6kg/c㎡，HDT | ASTM D648 | 249 ℃ |