| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Water absorption rate | 23℃，24hr | ISO 62 | 0.09 % |
| Shrinkage rate | | ASTM D-955 | 0.3-0.5 % |
| density | | ISO 1183 | 1.61 g/cm3 |
| processability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | | ISO 294-4 | 0.5-0.9 % |
| spiral flow length | | | -- cm |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | | ISO 527 | 115 MPa |
| elongation | Break | ISO 527 | 3.8 % |
| bending strength | | ISO 178 | 185 MPa |
| Flexural modulus | | ISO 178 | 7*103 MPa |
| Rockwell hardness | | ASTM D-785 | 90 M scale |
| elongation | | ASTM D-638 | 3.4 % |
| Impact strength of cantilever beam gap | 1/8" | ASTM D-256 | 50 J/m |
| tensile strength | | ASTM D-638 | 80 MPa |
| Flexural modulus | | ASTM D-790 | 5000 MPa |
| Charpy Notched Impact Strength | 无缺口 | ASTM D-256 | 25 KJ/M2 |
| Charpy Notched Impact Strength | Notched | ASTM D-256 | 7 KJ/M2 |
| bending strength | | ASTM D-790 | 105 MPa |
| Charpy Notched Impact Strength | Notched | ISO 179（leA） | 9 KJ/m2 |
| Flame retardant performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | | UL 94 | V-0（0.8mm） |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| dielectric constant | 106HZ | IEC 60250 | 3.4 |
| Dielectric loss | 106HZ，正切 | IEC 60250 | 1.8*10-2 |
| Volume resistivity | | ASTM D-257 | 1014 Ω.cm |
| dielectric constant | | ASTM D-150 | 3.0 106Hz |
| Dissipation Factor | | ASTM D-150 | 2.0×10-2 106Hz |
| dielectric strength | 2mm | ASTM D-149 | 23 MV/m |
| Volume resistivity | | IEC 60093 | 1*1014 Ω。m |
| dielectric strength | | IEC 60243 | 31 KV/m |
| arc resistance | | IEC 61621 | -- Sec |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| ash content | | | 30 % |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Hot deformation temperature (HDT) | 1.82MPa，HDT | ASTM D-648 | 170 ℃ |
| 线性热膨胀系数 | -30-30℃ | ASTM D-696 | 2.2 10-5℃mm/mm/℃ |
| UL flame retardant rating | 1/8-1/32" | UL 94 | HB V-0 |
| Hot deformation temperature (HDT) | 1.82MPa，HDT | ISO 75f | 195 ℃ |