Fluorelastomer

Fluorelastomer Greene FKM 929

0

برگه داده فنی

physical property شرایط آزمونروش آزموننتیجه آزمون
densityASTM D7921.85 g/cm³
hardnessشرایط آزمونروش آزموننتیجه آزمون
Shore hardnessShore AASTM D224097
Shore hardness邵氏DASTM D224065
Supplementary Informationشرایط آزمونروش آزموننتیجه آزمون
RubberClassificationFKM
tear strengthDie CASTM D62441.2 kN/m
elastomerشرایط آزمونروش آزموننتیجه آزمون
tensile strength BreakASTM D41218.0 MPa
elongationBreakASTM D41226 %
compression set100°C,70hrASTM D39534 %
compression set177°C,70hrASTM D39551 %
agingشرایط آزمونروش آزموننتیجه آزمون
Change rate of hardness (Shore) in the air邵氏A,100°C,70hrASTM D5730.0
Change rate of hardness (Shore) in the air支撐D,100°C,70hrASTM D573-3.0
Change rate of hardness (Shore) in the air邵氏A,177°C,70hrASTM D5730.0
Change rate of hardness (Shore) in the air支撐D,177°C,70hrASTM D573-4.0
Change rate of tensile strength in air100°C,70hr,在ASTM#1油中ASTM D471-2.0 %
Change rate of tensile strength in air100°C,70hr,在ASTM#3油中ASTM D471-4.8 %
Change rate of tensile strength in air177°C,70hr,在ASTM#3油中ASTM D471-11 %
Change rate of ultimate elongation in air100°C,70hr,在ASTM#1油中ASTM D47111 %
Change rate of ultimate elongation in air100°C,70hr,在ASTM#3油中ASTM D4718.6 %
Change rate of ultimate elongation in air177°C,70hr,在ASTM#3油中ASTM D47123 %
Change rate of hardness (Shore) in the air支撐A,100°C,70hr,在ASTM#3油中ASTM D4710.0
Change rate of hardness (Shore) in the air支撐D,100°C,70hr,在ASTM#3油中ASTM D471-5.0
Change rate of hardness (Shore) in the air支撐A,177°C,70hr,在ASTM#3油中ASTM D471-1.0
Change rate of hardness (Shore) in the air支撐D,177°C,70hr,在ASTM#3油中ASTM D471-7.0
volume change100°C,70hr,ASTM标准油（1号）ASTM D4710.80 %
volume change100°C,70hr,ASTM标准油（3号）ASTM D4711.1 %
volume change177°C,70hr,ASTM标准油（3号）ASTM D4713.2 %
Change rate of tensile strength in air100°C,70hrASTM D573-10 %
Change rate of tensile strength in air177°C,70hrASTM D573-5.0 %
Change rate of ultimate elongation in air100°C,70hrASTM D57311 %
Change rate of ultimate elongation in air177°C,70hrASTM D573-9.0 %
Change rate of hardness (Shore) in the air支撐A,100°C,70hr,在ASTM#1油中ASTM D4710.0
Change rate of hardness (Shore) in the air支撐D,100°C,70hr,在ASTM#1油中ASTM D471-5.0
Thermal performanceشرایط آزمونروش آزموننتیجه آزمون
Usage temperature-29-204 °C