impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	-40°C	ISO 179	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	13	kJ/m²
Impact strength of simply supported beam without notch	-40°C	ISO 179	60	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	65	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	0.79 mm	UL 94	HB
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Taber abraser	1000 Cycles	ISO 9352	0.400	mg
Friction coefficient - vs. Metal		Suzuki Method	0.15
shear strength	23°C	ASTM D732	95.0	Mpa
Compressive stress	80°C	ISO 604	110	Mpa
	Compressive stress	23°C	ISO 604	180	Mpa
	Compressive stress	Compressive stress	-40°C	ISO 604	250	Mpa
bending strength	80°C	ISO 178	190	Mpa
	bending strength	23°C	ISO 178	290	Mpa
	bending strength	bending strength	-40°C	ISO 178	325	Mpa
Bending modulus	80°C	ISO 178	5800	Mpa
	Bending modulus	23°C	ISO 178	9500	Mpa
	Bending modulus	Bending modulus	-40°C	ISO 178	11600	Mpa
Tensile strain	Break, 80°C	ISO 527-2	5.0	%
	Tensile strain	Break, 23°C	ISO 527-2	2.5	%
	Tensile strain	Tensile strain	Break, -40°C	ISO 527-2	2.0	%
tensile strength	80°C	ISO 527-2	120	Mpa
	tensile strength	23°C	ISO 527-2	190	Mpa
	tensile strength	tensile strength	-40°C	ISO 527-2	235	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	262	°C
Melting temperature		DSC	265	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.0E-5 - 3.0E-5	cm/cm/°C
specific heat			1800	J/kg/°C
thermal conductivity			0.40	W/m/K
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate	Flow : 3.00 mm	Internal Method	0.20 - 0.50	%
Shrinkage rate	Shrinkage rate	横向Flow : 3.00 mm	Internal Method	0.60 - 0.90	%
density	23°C	ISO 1183	1.37	g/cm³
Water absorption rate	Saturation, 23°C	ISO 62	5.5	%
Water absorption rate	Water absorption rate	24 hr, 23°C	ISO 62	0.60	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Volume resistivity		IEC 60093	1.0E+13	ohms·cm
Dielectric strength		IEC 60243-1	20	KV/mm
Dielectric constant	23°C, 50 Hz	IEC 60250	4.60
	Dielectric constant	23°C, 1 kHz	IEC 60250	4.40
	Dielectric constant	Dielectric constant	23°C, 1 MHz	IEC 60250	3.90
Dissipation factor	23°C, 50 Hz	IEC 60250	0.020
	Dissipation factor	23°C, 1 kHz	IEC 60250	0.020
	Dissipation factor	Dissipation factor	23°C, 1 MHz	IEC 60250	0.020
Arc resistance		UL 746	114	sec
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	R -Sale, 23°C	ISO 2039-2	121
	Rockwell hardness	R -Sale, 80°C	ISO 2039-2	24
	Rockwell hardness	Rockwell hardness	M -Sale, 23°C	ISO 2039-2	97