| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTMD792 | 1.16to1.18 g/cm³ |
| Shrinkage rate | MD | ASTM D955 | 1.0to1.5 % |
| Shrinkage rate | TD | ASTM D955 | 1.5to2.5 % |
| Water absorption rate | 23°C,24hr | ASTMD570 | 1.0to1.5 % |
| Water absorption rate | Saturation | ASTM D570 | 8.0 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 8.0 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Burning wire flammability index | 1.2mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.2mm | IEC 60695-2-13 | 775 °C |
| Limiting Oxygen Index | | ASTM D2863 | 32 % |
| UL flame retardant rating | 0.55mm | UL 94 | V-0 |
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| UL flame retardant rating | 3.2mm | UL 94 | V-0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ASTMD638 | 3600 MPa |
| tensile strength | Yield | ASTMD638 | 95.0 MPa |
| tensile strength | Break | ASTMD638 | 85.0 MPa |
| elongation | Break | ASTMD638 | 6.0 % |
| Flexural modulus | | ASTMD790 | 3300 MPa |
| bending strength | -- | ISO 178 | 135 MPa |
| bending strength | Break | ASTM D790 | 135 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 50 kJ/m² |
| Impact strength of cantilever beam gap | -20°C,3.20mm | ASTMD256 | 25 J/m |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 40 J/m |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 2.5 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | 1E+15 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ASTMD648 | 225 °C |
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ASTMD648 | 90.0 °C |
| Continuous use temperature | --4 | IEC 60216 | 80.0 °C |
| Continuous use temperature | --5 | IEC 60216 | 120 °C |
| vicat | -- | ASTMD15256 | 248 °C |
| vicat | -- | ASTMD15257 | 236 °C |
| melting temperature | | ASTMD211 | 250to256 °C |
| 线性热膨胀系数 | MD：-30到30°C | ASTM D696 | 8E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.