برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Water absorption rate | 饱和,23°C | ISO 62 | 0.30 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.10 % |
| Shrinkage rate | TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.20 % |
| Shrinkage rate | MD:270°C,2.00mm2 | ISO 294-4 | 0.30 % |
| Shrinkage rate | MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.10 % |
| density | 23°C | ISO 1183 | 1.55 g/cm³ |
| Apparent density | | ISO 60 | 0.80 g/cm³ |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 30.0 cm³/10min |
| Shrinkage rate | TD:270°C,2.00mm2 | ISO 294-4 | 0.90 % |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| ISO Shortcut | | ISO 7792 | PBT+PET.GHMR.09-100.GF30 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 23°C | ISO 527-2/1 | 10400 MPa |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 145 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 2.8 % |
| Flexural modulus | 23°C | ISO 178/A | 10300 MPa |
| bending strength | 23°C | ISO 178 | 230 MPa |
| Bending Strain | 23°C | | 3.0 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | <10 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | <10 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 55 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 65 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | <10 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | <10 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 55 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 55 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ISO 75-2/A | 200 °C |
| vicat | | ISO 306/B120 | 205 °C |
| melting temperature | | ISO 11357-3 | 225to250 °C |
| 线性热膨胀系数 | MD：23到55°C | ISO 11359-2 | 3E-05 cm/cm/°C |
| 线性热膨胀系数 | TD：23to55°C | ISO 11359-2 | 9E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.
مقایسه