MPR 4080 BK USA Advanced

کاربردها:
Encapsulation molding universal fabric coating gaskets seals fittings cable sheaths handles wire and cable applications weather resistant sealing strips pipes profiles coating applications soft handles
مقایسه

برگه داده فنی

elastomer	شرایط آزمون	روش آزمون	نتیجه آزمون
elongation	Break,125°C,1.90mm4	ISO 188	380 %
	elongation	Break,1.90mm2	ISO 37	380 %
		elongation	Break,1.90mm2	ASTM D412	380 %
		elongation	elongation	Break,125°C,1.90mm4	ASTM D573	380 %
tensile strength	Yield,125°C,1.90mm4	ISO 188	11.0 MPa
	tensile strength	Yield,1.90mm2	ISO 37	10.8 MPa
	tensile strength	tensile strength	Yield,125°C,1.90mm4	ASTM D573	11.0 MPa
Permanent compression deformation	100°C,22hr	ASTM D395B	75 %
Permanent compression deformation	Permanent compression deformation	24°C,22hr	ASTM D395B	24 %
tear strength	1.90mm	ASTM D624	52.5 kN/m
Permanent compression deformation	24°C,22hr	ISO 815	24 %
Permanent compression deformation	Permanent compression deformation	100°C,22hr	ISO 815	75 %
Clash Mountain Module	1°C	ASTM D1043	68.9 MPa
Stretch permanent deformation		ASTM D412	12 %
tensile strength	100%Strain,1.90mm2	ASTM D412	5.90 MPa
	tensile strength	100%Strain,125°C,1.90mm4	ASTM D573	7.50 MPa
		tensile strength	100%Strain,1.90mm2	ISO 37	5.90 MPa
			tensile strength	100%Strain,125°C,1.90mm4	ISO 188	7.50 MPa
			tensile strength	tensile strength	Yield,1.90mm2	ASTM D412	10.8 MPa

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
TorsionModulus	-20°C,1.90mm	ASTM D1043	68.9 MPa
Taber abraser	1000Cycles,1000g,CS-17Wheel	ASTM D1044	6.00 mg
TorsionModulus	24°C,1.90mm	ASTM D1043	4.10 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Brittle temperature		ASTM D746	-58.0 °C
Brittle temperature	Brittle temperature		ISO 812	-58.0 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ISO 2781	1.27 g/cm³
density	density		ASTM D471	1.27 g/cm³
MeltViscosity	190°C,300sec^-1	ASTM D3835	780 Pa·s

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
DurometerHardness	ShoreA,1.90mm,CompressionMolded	ASTM D2240	79
Shore hardness	ShoreA,1.90mm,CompressionMolded	ISO 868	79

aging	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume change	100°C,168hr,inASTM#1Oil	ISO 1817	-9.0 %
	Volume change	27°C,168hr,inReferenceFuelB	ISO 1817	22 %
		Volume change	100°C,168hr,在水中	ASTM D471	10 %
			Volume change	100°C,168hr,inIRM903Oil	ASTM D471	24 %
				Volume change	100°C,168hr,inASTM#1Oil	ASTM D471	-9.0 %
				Volume change	Volume change	27°C,168hr,inReferenceFuelB	ASTM D471	22 %
Shore hardness	ShoreA,125°C,168hr	ISO 188	-3.0
Hardness change rate in the air	ShoreA,125°C,168hr	ASTM D573	-3.0
Volume change	100°C,168hr,在水中	ISO 1817	10 %
Volume change	Volume change	100°C,168hr,inIRM903Oil	ISO 1817	24 %

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.