HIPS SEHI-110 IDEMITSU MALASIA

ویژگی‌ها:
Characteristics high impact resistance good fluidity flame retardant form particles
کاربردها:
Shell
مقایسه

برگه داده فنی

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	3.00 mm	UL 94	V-0

squeeze out	شرایط آزمون	روش آزمون	نتیجه آزمون
Oral mold temperature			190 to 220 °C
drying temperature			70.0 °C
drying time			1.0 to 2.0 hr
Material barrel temperature			160 to 200 °C
	Material barrel temperature			180 to 220 °C
		Material barrel temperature			200 to 240 °C
		Material barrel temperature	Material barrel temperature			200 to 240 °C

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Break	ASTM D638	26.0 MPa
elongation	Break	ASTM D638	38 %

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			70.0 °C
drying time			1.0 to 2.0 hr
Temperature at the rear of the barrel			180 to 210 °C
Temperature in the middle of the barrel			190 to 220 °C
Temperature at the front of the material cylinder			210 to 240 °C
Spray nozzle temperature			200 to 230 °C
Mold temperature			40.0 to 60.0 °C

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	70.0 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.15 g/cm³
melt mass-flow rate	200°C/5.0 kg	ASTM D1238	11 g/10 min

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.