برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| water content | | ISO 960 | <1000 ppm |
| density | | ISO 1183 | 1.26 g/cm³ |
| melt mass-flow rate | 270°C/2.16kg | ISO 1133 | 100 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| density | | ISO 1183 | 1.26 g/cm³ |
| melt mass-flow rate | 270°C/2.16 kg | ISO 1133 | 100 g/10 min |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.20 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 650 °C |
| UL flame retardant rating | 3.20 mm | UL 94 | HB |
| Burning wire flammability index | 2.00 mm | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | 1.60 mm | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 23°C | ISO 527-2/5 | 1750 MPa |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 45.0 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 25 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Tensile modulus | 23°C | ISO 527-2/5 | 1750 MPa |
| tensile strength | 断裂, 23°C | ISO 527-2/5 | 45 MPa |
| Tensile strain | 断裂, 23°C | ISO 527-2/5 | 25 % |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | -20°C | ISO 180/1A | 7.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | -20°C | ISO 180/1A | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 1E+14 ohms |
| Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melting temperature | | ISO 11357 | 225 °C |
| melting temperature | | ISO 11357 | 225 °C |
| Electrical performance | 表面电阻率 | IEC 60093 | 1E+03 ohms |
| Volume resistivity | | IEC 60093 | 1E+03 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |