| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 0.904 g/cm³ |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 4.0 g/10min |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| transparency | | ASTM D-1746 | 99 |
| gloss | 45° | ASTM D-2457 | 90 |
| Haze ratio | | ASTM D-1003 | 1.8 % |
| gloss | 45°,20.3µm | ASTM D2457 | 92 |
| gloss | 45°,50.8µm | ASTM D2457 | 90 |
| transparency | 20.3µm | ASTM D1746 | 99.0 |
| transparency | 50.8µm | ASTM D1746 | 99.0 |
| Haze ratio | 20.3µm | ASTM D1003 | 0.60 % |
| Haze ratio | 50.8µm | ASTM D1003 | 1.8 % |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | | ASTM D1238 | 4 g/10min |
| density | | ASTM D792 | 0.904 g/cm3 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| elongation at break | MD | ASTM D-882 | 664 % |
| Tensile modulus | TD | ASTM D-882 | 63 MPa |
| Tensile modulus | MD | ASTM D-882 | 63 MPa |
| Puncture Strength | | 陶氏企业测试 | 17 J/cm3 |
| tensile strength | 屈服,TD | ASTM D-882 | 5 MPa |
| tensile strength | 屈服,MD | ASTM D-882 | 7 MPa |
| tensile strength | TD，断裂 | ASTM D-882 | 32 MPa |
| tensile strength | MD，断裂 | ASTM D-882 | 33 MPa |
| elongation at break | TD | ASTM D-882 | 714 % |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Thin film puncture strength | 20µm | 内部方法 | 18.9 J/cm³ |
| Thin film puncture strength | 51µm | 内部方法 | 17.5 J/cm³ |
| Secant modulus | 2%正割,MD:20µm | ASTM D882 | 58.8 MPa |
| Secant modulus | 2%正割,MD:51µm | ASTM D882 | 62.6 MPa |
| Secant modulus | 2%正割,TD:20µm | ASTM D882 | 64.7 MPa |
| Secant modulus | 2%正割,TD:51µm | ASTM D882 | 63.0 MPa |
| tensile strength | MD:屈服,20µm | ASTM D882 | 7.00 MPa |
| tensile strength | MD:屈服,51µm | ASTM D882 | 6.76 MPa |
| tensile strength | TD:屈服,20µm | ASTM D882 | 4.92 MPa |
| tensile strength | TD:屈服,51µm | ASTM D882 | 6.34 MPa |
| tensile strength | MD:断裂,20µm | ASTM D882 | 36.9 MPa |
| tensile strength | MD:断裂,51µm | ASTM D882 | 32.6 MPa |
| tensile strength | TD:断裂,20µm | ASTM D882 | 29.1 MPa |
| tensile strength | TD:断裂,51µm | ASTM D882 | 32.4 MPa |
| elongation | TD:断裂,51µm | ASTM D882 | 710 % |
| Dart impact | 20µm | ASTM D1709B | >850 g |
| Dart impact | 51µm | ASTM D1709B | >850 g |
| Elmendorf tear strength | MD:20µm | ASTM D1922 | 330 g |
| Elmendorf tear strength | MD:51µm | ASTM D1922 | 960 g |
| elongation | MD:断裂,20µm | ASTM D882 | 500 % |
| elongation | MD:断裂,51µm | ASTM D882 | 660 % |
| elongation | TD:断裂,20µm | ASTM D882 | 710 % |
| Elmendorf tear strength | TD:20µm | ASTM D1922 | 500 g |
| Elmendorf tear strength | TD:51µm | ASTM D1922 | 1100 g |
| OTr | 23°C,51µm | ASTM D3985 | 450 cm³·mm/m²/atm/24hr |
| Water Vapor Transmission Rate | 51µm | ASTMF1249 | 0.85 g·mm/m²/atm/24hr |
| Carbon dioxide transmittance | 23°C,50.8µm | 内部方法 | 2000 cm³·mm/m²/atm/24hr |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| vicat | | ASTM D1525 | 71.1 °C |
| melting temperature | | 内部方法 | 124 °C |
| vicat | | ASTM D-1525 | 71 ℃ |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.